BARIUM AND CALCIUM NIOBATE CERAMICS: SPECIFIC FEATURES OF THEIR STRUCTURE
We obtained and studied the samples of ceramics based on barium niobate and calcium niobate CaxBa1-xNb2O6 with different percentages of barium and calcium (x=1; 0,9; 0,8; 0,7; 0,6; 0,5; 0,4; 0,3; 0,2; 0,1 and 0). The effect of the sintering temperature on the structure and dielectric properties of c...
Guardado en:
| Autores principales: | , , , |
|---|---|
| Formato: | article |
| Lenguaje: | RU |
| Publicado: |
Tver State University
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/013a223fb8c648ccb4261f89d439672a |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | We obtained and studied the samples of ceramics based on barium niobate and calcium niobate CaxBa1-xNb2O6 with different percentages of barium and calcium (x=1; 0,9; 0,8; 0,7; 0,6; 0,5; 0,4; 0,3; 0,2; 0,1 and 0). The effect of the sintering temperature on the structure and dielectric properties of ceramics has been investigated. One batch of the samples was sintered at a temperature of 1100°C, the second at 1250°C. We have shown that the sintering temperature of 1100°C is not enough to obtain good ferroelectric properties, and the process of grain recrystallization is not completed. According to studies of the elemental composition, in samples sintered at a temperature of 1250°C with the Ca content greater than 0,5, Ba atoms are not present in all grains, which also affects the course of the temperature dependences of the dielectric constant A sample with x=0,3 is distinguished by its dielectric properties. |
|---|