Laws Governing Free and Actual Drying Shrinkage of 50 mm Thick Mongolian Scotch Pine Timber
The relationships between free shrinkage and actual shrinkage of different layers in Mongolian Scotch pine (Pinus sylvestris var. mongolica Litv.) were explored to provide basic data for the further study of drying shrinkage properties. The free shrinkage coefficients at different temperatures and t...
Guardado en:
| Autores principales: | , , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
MDPI AG
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/03572ccc90c84c0d912efcdf8800d8a1 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | The relationships between free shrinkage and actual shrinkage of different layers in Mongolian Scotch pine (Pinus sylvestris var. mongolica Litv.) were explored to provide basic data for the further study of drying shrinkage properties. The free shrinkage coefficients at different temperatures and the actual shrinkage strain of each layer were examined under conventional drying. The results showed high precision of free drying shrinkage of corresponding layers of thin small test strips in each layer of sawn timber. The free shrinkage increased linearly as moisture content declined. At the same temperature, the free shrinkage coefficient reached the largest values for the first layer (above 0.267%), while the smallest values were recorded for the ninth layer (below 0.249%). Except for the ninth layer, the free shrinkage coefficients in width directions of other representative layers decreased as temperature increased. At constant temperature, the difference in free shrinkage coefficient of test materials in the length direction of sawn timber was small for the first layer, but slightly larger and changed irregularly in the fifth and ninth layer direction. At the end of conventional drying, the plastic deformation of each layer in the early stage of drying showed a reducing trend or even reversal due to the effects of reverse stress and later damp heat. In sum, these findings look promising for future optimization of wood drying process. |
|---|