Modeling studies of corrosion fatigue in a low carbon steel
This paper presents the results of the modeling studies of the simultaneous action of applied cyclic stress and the corrosion of low-carbon steel in environments with different pH levels (pH of 3, 5, 8, and 11). The evolution of fatigue cracks from corrosion pits is explored using scanning electron...
Guardado en:
Autores principales: | S. K. Kolawole, F. O. Kolawole, A. B. O. Soboyejo, W. O. Soboyejo |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
Taylor & Francis Group
2019
|
Materias: | |
Acceso en línea: | https://doaj.org/article/0647d8ea55fb454ba035907902bfc8a5 |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares
-
Analysis of the pit geometry influence on the rupture by corrosion-fatigue in Zr55Al10Cu30Ni5 bulk metallic glass exposed to distilled water medium
por: Benjamin GUENNEC, et al.
Publicado: (2021) -
Atmospheric Corrosion Behavior of Carbon Steel and Galvanized Steel after Exposure in Eretan and Ciwaringin, West Java Province, Indonesia
por: Gadang Priyotomo, et al.
Publicado: (2020) -
Subjective approach to optimal cross-sectional design of biodegradable magnesium alloy stent undergoing heterogeneous corrosion
por: Najmeh Zarei, et al.
Publicado: (2021) -
Research on the Corrosion Fatigue Property of 2524-T3 Aluminum Alloy
por: Chi Liu, et al.
Publicado: (2021) -
Heating impact on corrosion mechanism of carbon steel surrounded by bentonite
por: Masao UYAMA, et al.
Publicado: (2021)