Characterization of the Strain-Rate-Dependent Plasticity of Alloys Using Instrumented Indentation Tests
Instrumented indentation tests are an efficient approach for the characterization of stress–strain curves instead of tensile or compression tests and have recently been applied for the evaluation of mechanical properties at elevated temperatures. In high-temperature tests, the rate dependence of the...
Guardado en:
| Autores principales: | , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
MDPI AG
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/06c6a348c6e045518f33ff85b1e5518b |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Instrumented indentation tests are an efficient approach for the characterization of stress–strain curves instead of tensile or compression tests and have recently been applied for the evaluation of mechanical properties at elevated temperatures. In high-temperature tests, the rate dependence of the applied load appears to be dominant. In this study, the strain-rate-dependent plasticity in instrumented indentation tests at high temperatures was characterized through the assimilation of experiments with a simulation model. Accordingly, a simple constitutive model of strain-rate-dependent plasticity was defined, and the material constants were determined to minimize the difference between the experimental results and the corresponding simulations at a constant high temperature. Finite element simulations using a few estimated mechanical properties were compared with the corresponding experiments in compression tests at the same temperature for the validation of the estimated material responses. The constitutive model and determined material constants can reproduce the strain-rate-dependent material behavior under various loading speeds in instrumented indentation tests; however, the load level of computational simulations is lower than those of the experiments in the compression tests. These results indicate that the local mechanical responses evaluated in the instrumented indentation tests were not consistent with the bulk responses in the compression tests at high temperature. Consequently, the bulk properties were not able to be characterized using instrumented indentation tests at high temperature because of the scale effect. |
|---|