Comparative Study of the Mechanical Properties of (FS) and MIG Welded Joint in (AA7020-T6) Aluminum Alloy

A comprehensive practical study of typical mechanical properties of welded Aluminum alloy AA7020-T6 (Al-Mg-Zn), adopting friction stir welding (FSW) technique and conventional metal inert gas (MIG) technique, is well achieved in this work for real comparison purposes. The essences of present output...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Zainab Waheed, Kadhim M. Mashloosh, Moneer Hammed Tolephih
Formato: article
Lenguaje:EN
Publicado: Al-Khwarizmi College of Engineering – University of Baghdad 2011
Materias:
Acceso en línea:https://doaj.org/article/0b512bf4525e4ce0b3af17ca611dabae
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
id oai:doaj.org-article:0b512bf4525e4ce0b3af17ca611dabae
record_format dspace
spelling oai:doaj.org-article:0b512bf4525e4ce0b3af17ca611dabae2021-12-02T05:40:28ZComparative Study of the Mechanical Properties of (FS) and MIG Welded Joint in (AA7020-T6) Aluminum Alloy1818-1171https://doaj.org/article/0b512bf4525e4ce0b3af17ca611dabae2011-01-01T00:00:00Zhttp://www.iasj.net/iasj?func=fulltext&aId=2341https://doaj.org/toc/1818-1171A comprehensive practical study of typical mechanical properties of welded Aluminum alloy AA7020-T6 (Al-Mg-Zn), adopting friction stir welding (FSW) technique and conventional metal inert gas (MIG) technique, is well achieved in this work for real comparison purposes. The essences of present output findings were concentrated upon the FSW samples in respect to that MIG ones which can be summarized in the increase of the ultimate tensile strength for FSW was 340 MPa while it was 232 MPa for MIG welding, where it was for base metal 400 MPa. The minimum microhardness value for FSW was recorded at HAZ and it was 133 HV0.05 while it was 70 HV0.05 for MIG weld at the welding metal. The FSW produce 2470 N higher than MIG welding in the bending test and a decrease in the localized grain size for FSW in the stirred zone 12 µm and it was 37 µm for MIG while it was 32 µm for the base metalZainab WaheedKadhim M. MashlooshMoneer Hammed TolephihAl-Khwarizmi College of Engineering – University of BaghdadarticleFSW frictionstir weldingsolid stateMIG metal inert gasfusionmechanical properties.Chemical engineeringTP155-156Engineering (General). Civil engineering (General)TA1-2040ENAl-Khawarizmi Engineering Journal, Vol 7, Iss 2, Pp 22-35 (2011)
institution DOAJ
collection DOAJ
language EN
topic FSW friction
stir welding
solid state
MIG metal inert gas
fusion
mechanical properties.
Chemical engineering
TP155-156
Engineering (General). Civil engineering (General)
TA1-2040
spellingShingle FSW friction
stir welding
solid state
MIG metal inert gas
fusion
mechanical properties.
Chemical engineering
TP155-156
Engineering (General). Civil engineering (General)
TA1-2040
Zainab Waheed
Kadhim M. Mashloosh
Moneer Hammed Tolephih
Comparative Study of the Mechanical Properties of (FS) and MIG Welded Joint in (AA7020-T6) Aluminum Alloy
description A comprehensive practical study of typical mechanical properties of welded Aluminum alloy AA7020-T6 (Al-Mg-Zn), adopting friction stir welding (FSW) technique and conventional metal inert gas (MIG) technique, is well achieved in this work for real comparison purposes. The essences of present output findings were concentrated upon the FSW samples in respect to that MIG ones which can be summarized in the increase of the ultimate tensile strength for FSW was 340 MPa while it was 232 MPa for MIG welding, where it was for base metal 400 MPa. The minimum microhardness value for FSW was recorded at HAZ and it was 133 HV0.05 while it was 70 HV0.05 for MIG weld at the welding metal. The FSW produce 2470 N higher than MIG welding in the bending test and a decrease in the localized grain size for FSW in the stirred zone 12 µm and it was 37 µm for MIG while it was 32 µm for the base metal
format article
author Zainab Waheed
Kadhim M. Mashloosh
Moneer Hammed Tolephih
author_facet Zainab Waheed
Kadhim M. Mashloosh
Moneer Hammed Tolephih
author_sort Zainab Waheed
title Comparative Study of the Mechanical Properties of (FS) and MIG Welded Joint in (AA7020-T6) Aluminum Alloy
title_short Comparative Study of the Mechanical Properties of (FS) and MIG Welded Joint in (AA7020-T6) Aluminum Alloy
title_full Comparative Study of the Mechanical Properties of (FS) and MIG Welded Joint in (AA7020-T6) Aluminum Alloy
title_fullStr Comparative Study of the Mechanical Properties of (FS) and MIG Welded Joint in (AA7020-T6) Aluminum Alloy
title_full_unstemmed Comparative Study of the Mechanical Properties of (FS) and MIG Welded Joint in (AA7020-T6) Aluminum Alloy
title_sort comparative study of the mechanical properties of (fs) and mig welded joint in (aa7020-t6) aluminum alloy
publisher Al-Khwarizmi College of Engineering – University of Baghdad
publishDate 2011
url https://doaj.org/article/0b512bf4525e4ce0b3af17ca611dabae
work_keys_str_mv AT zainabwaheed comparativestudyofthemechanicalpropertiesoffsandmigweldedjointinaa7020t6aluminumalloy
AT kadhimmmashloosh comparativestudyofthemechanicalpropertiesoffsandmigweldedjointinaa7020t6aluminumalloy
AT moneerhammedtolephih comparativestudyofthemechanicalpropertiesoffsandmigweldedjointinaa7020t6aluminumalloy
_version_ 1718400274871091200