Manufacturing of biodegradable polyurethane scaffolds based on polycaprolactone using a phase separation method: physical properties and in vitro assay

Azadeh Asefnejad1, Mohammad Taghi Khorasani2, Aliasghar Behnamghader3, Babak Farsadzadeh1, Shahin Bonakdar4 1Department of Biomedical Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran; 2Iran Polymers and Petrochemical Institute, Tehran, Iran; 3Materials and Energy Resea...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Asefnejad A, Khorasani MT, Behnamghader A, Farsadzadeh B, Bonakdar S
Formato: article
Lenguaje:EN
Publicado: Dove Medical Press 2011
Materias:
Acceso en línea:https://doaj.org/article/0effe3e9eb434dbc951f0599c1c1c3e3
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
Descripción
Sumario:Azadeh Asefnejad1, Mohammad Taghi Khorasani2, Aliasghar Behnamghader3, Babak Farsadzadeh1, Shahin Bonakdar4 1Department of Biomedical Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran; 2Iran Polymers and Petrochemical Institute, Tehran, Iran; 3Materials and Energy Research Center, Tehran, Iran; 4National Cell Bank of Iran, Pasteur Institute of Iran, Tehran, Iran Background: Biodegradable polyurethanes have found widespread use in soft tissue engineering due to their suitable mechanical properties and biocompatibility. Methods: In this study, polyurethane samples were synthesized from polycaprolactone, hexamethylene diisocyanate, and a copolymer of 1,4-butanediol as a chain extender. Polyurethane scaffolds were fabricated by a combination of liquid–liquid phase separation and salt leaching techniques. The effect of the NCO:OH ratio on porosity content and pore morphology was investigated. Results: Scanning electron micrographs demonstrated that the scaffolds had a regular distribution of interconnected pores, with pore diameters of 50–300 µm, and porosities of 64%–83%. It was observed that, by increasing the NCO:OH ratio, the average pore size, compressive strength, and compressive modulus increased. L929 fibroblast and chondrocytes were cultured on the scaffolds, and all samples exhibited suitable cell attachment and growth, with a high level of biocompatibility. Conclusion: These biodegradable polyurethane scaffolds demonstrate potential for soft tissue engineering applications. Keywords: polyurethane, tissue engineering, biodegradable, fibroblast cells