Characterization of microscopic damage due to low-velocity and high-velocity impact in CFRP with toughened interlayers
In this paper the low-velocity and high-velocity impact damage in a carbon fiber reinforced plastic (CFRP) laminate with toughened interlayers was experimentally characterized. The low-velocity impact test was carried out by using a guided drop weight system while the high-velocity impact test was c...
Guardado en:
Autores principales: | Rozaini OTHMAN, Keiji OGI, Shigeki YASHIRO |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
The Japan Society of Mechanical Engineers
2016
|
Materias: | |
Acceso en línea: | https://doaj.org/article/0f98a935eb874987a3928de85c27d1f4 |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares
-
An experimental study on damage intensity in composite plates subjected to low-velocity impacts
por: Sajjad Seifoori, et al.
Publicado: (2021) -
Effects of structural defects on low-velocity impact damage mechanisms of three-dimensional braided composites based on X-ray micro-computed tomography
por: Mengyao Sun, et al.
Publicado: (2021) -
Damage mechanism of CFRP laminates with different curvatures impacted by ice projectile at high velocity
por: Enling Tang, et al.
Publicado: (2021) -
On the Low-Velocity Impact Response of Laminated Glass with Different Types of Glass and Interlayers
por: Alena Zemanová, et al.
Publicado: (2020) -
Combined loadings after medium velocity impact on large CFRP laminated plates: Discrete ply model simulations
por: J. Serra, et al.
Publicado: (2021)