Evaluation of the microstructural and mechanical properties of ductile cast iron and alloy steel dissimilar materials welded by magnetically impelled arc butt
The combined use of ductile cast iron and alloy steel is beneficial, however, this technique causes some difficulties in welding due to the different properties of these two materials. In the present work, magnetically impelled arc butt (MIAB) welding a solid-state joining process, was employed to w...
Guardado en:
Autores principales: | , , , , , |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
Elsevier
2021
|
Materias: | |
Acceso en línea: | https://doaj.org/article/1348cf2fde8d45d182bad25b6c24e05c |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
id |
oai:doaj.org-article:1348cf2fde8d45d182bad25b6c24e05c |
---|---|
record_format |
dspace |
spelling |
oai:doaj.org-article:1348cf2fde8d45d182bad25b6c24e05c2021-11-04T04:31:45ZEvaluation of the microstructural and mechanical properties of ductile cast iron and alloy steel dissimilar materials welded by magnetically impelled arc butt2238-785410.1016/j.jmrt.2021.10.059https://doaj.org/article/1348cf2fde8d45d182bad25b6c24e05c2021-11-01T00:00:00Zhttp://www.sciencedirect.com/science/article/pii/S2238785421011959https://doaj.org/toc/2238-7854The combined use of ductile cast iron and alloy steel is beneficial, however, this technique causes some difficulties in welding due to the different properties of these two materials. In the present work, magnetically impelled arc butt (MIAB) welding a solid-state joining process, was employed to weld GGG40 ductile cast iron tube and an E355 + N alloy steel tube (each one had a thickness of 6 mm). The microstructure and mechanical properties of the resultant joints along different positions of the weld tube were systematically investigated. The heating during MIAB welding was non-uniform, causing significant changes in the microstructure, microhardness, and tensile stress of the welds. The maximum hardness of the welds (482 HV) was much higher than that of the base metal. The average (334.4 MPa) and maximum tensile strengths (382.4 MPa) of the welds were 83.6% and 95.6% of those of the base metal, respectively. These results show that MIAB is an effective method for welding ductile cast iron/alloy steel dissimilar materials.Mingjian PengHongbing LiuYang XuanXu LiuLei XuZhishui YuElsevierarticleMagnetically impelled arc butt weldingDuctile cast ironAlloy steelDissimilar material weldWelding propertyMining engineering. MetallurgyTN1-997ENJournal of Materials Research and Technology, Vol 15, Iss , Pp 4623-4635 (2021) |
institution |
DOAJ |
collection |
DOAJ |
language |
EN |
topic |
Magnetically impelled arc butt welding Ductile cast iron Alloy steel Dissimilar material weld Welding property Mining engineering. Metallurgy TN1-997 |
spellingShingle |
Magnetically impelled arc butt welding Ductile cast iron Alloy steel Dissimilar material weld Welding property Mining engineering. Metallurgy TN1-997 Mingjian Peng Hongbing Liu Yang Xuan Xu Liu Lei Xu Zhishui Yu Evaluation of the microstructural and mechanical properties of ductile cast iron and alloy steel dissimilar materials welded by magnetically impelled arc butt |
description |
The combined use of ductile cast iron and alloy steel is beneficial, however, this technique causes some difficulties in welding due to the different properties of these two materials. In the present work, magnetically impelled arc butt (MIAB) welding a solid-state joining process, was employed to weld GGG40 ductile cast iron tube and an E355 + N alloy steel tube (each one had a thickness of 6 mm). The microstructure and mechanical properties of the resultant joints along different positions of the weld tube were systematically investigated. The heating during MIAB welding was non-uniform, causing significant changes in the microstructure, microhardness, and tensile stress of the welds. The maximum hardness of the welds (482 HV) was much higher than that of the base metal. The average (334.4 MPa) and maximum tensile strengths (382.4 MPa) of the welds were 83.6% and 95.6% of those of the base metal, respectively. These results show that MIAB is an effective method for welding ductile cast iron/alloy steel dissimilar materials. |
format |
article |
author |
Mingjian Peng Hongbing Liu Yang Xuan Xu Liu Lei Xu Zhishui Yu |
author_facet |
Mingjian Peng Hongbing Liu Yang Xuan Xu Liu Lei Xu Zhishui Yu |
author_sort |
Mingjian Peng |
title |
Evaluation of the microstructural and mechanical properties of ductile cast iron and alloy steel dissimilar materials welded by magnetically impelled arc butt |
title_short |
Evaluation of the microstructural and mechanical properties of ductile cast iron and alloy steel dissimilar materials welded by magnetically impelled arc butt |
title_full |
Evaluation of the microstructural and mechanical properties of ductile cast iron and alloy steel dissimilar materials welded by magnetically impelled arc butt |
title_fullStr |
Evaluation of the microstructural and mechanical properties of ductile cast iron and alloy steel dissimilar materials welded by magnetically impelled arc butt |
title_full_unstemmed |
Evaluation of the microstructural and mechanical properties of ductile cast iron and alloy steel dissimilar materials welded by magnetically impelled arc butt |
title_sort |
evaluation of the microstructural and mechanical properties of ductile cast iron and alloy steel dissimilar materials welded by magnetically impelled arc butt |
publisher |
Elsevier |
publishDate |
2021 |
url |
https://doaj.org/article/1348cf2fde8d45d182bad25b6c24e05c |
work_keys_str_mv |
AT mingjianpeng evaluationofthemicrostructuralandmechanicalpropertiesofductilecastironandalloysteeldissimilarmaterialsweldedbymagneticallyimpelledarcbutt AT hongbingliu evaluationofthemicrostructuralandmechanicalpropertiesofductilecastironandalloysteeldissimilarmaterialsweldedbymagneticallyimpelledarcbutt AT yangxuan evaluationofthemicrostructuralandmechanicalpropertiesofductilecastironandalloysteeldissimilarmaterialsweldedbymagneticallyimpelledarcbutt AT xuliu evaluationofthemicrostructuralandmechanicalpropertiesofductilecastironandalloysteeldissimilarmaterialsweldedbymagneticallyimpelledarcbutt AT leixu evaluationofthemicrostructuralandmechanicalpropertiesofductilecastironandalloysteeldissimilarmaterialsweldedbymagneticallyimpelledarcbutt AT zhishuiyu evaluationofthemicrostructuralandmechanicalpropertiesofductilecastironandalloysteeldissimilarmaterialsweldedbymagneticallyimpelledarcbutt |
_version_ |
1718445255308607488 |