Characteristics of Hydrochar and Liquid Products Obtained by Hydrothermal Carbonization and Wet Torrefaction of Poultry Litter in Mixture with Wood Sawdust
Poultry farms with floor-standing poultry generate large amounts of poultry litter waste. The direct application of this waste as an organic fertilizer does not ensure sustainable and cost-efficient utilization of all waste fractions, and can also be linked to environmental hazards. Therefore, the d...
Guardado en:
| Autores principales: | , , , , , , , , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
MDPI AG
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/162a5a8d1e654a3c936bf4d7ce5394de |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Poultry farms with floor-standing poultry generate large amounts of poultry litter waste. The direct application of this waste as an organic fertilizer does not ensure sustainable and cost-efficient utilization of all waste fractions, and can also be linked to environmental hazards. Therefore, the development of new technologies is required for processing poultry litter into a safe product with higher added value. In this work, the characteristics of activated carbon derived from hydrochar, along with the liquid products obtained from hydrothermal carbonization (HTC) and the wet torrefaction (WT) of poultry litter, were investigated. Poultry litter (PL) was applied in a mixture with sawdust (SD) in the following ratios: 1:0 (PL/SD 1:0), 1:1 (PL/SD 1:1), 1:2 (PL/SD 1:2), and 2:1 (PL/SD 2:1). WT processing took place in an innovative fluidized bed system in a superheated steam medium with low overpressure (less than 0.07 MPa) at 300 °C and 350 °C for 30–45 min. Conventional HTC processing was performed in a water medium at 220 °C for 1–4 h. The hydrochar produced in the experiments was activated with steam for 1 h at 450–750 °C. The porosity characteristics of activated hydrochar were measured, including pore size, pore volume, and specific surface area, in view of potential industrial applications as an adsorbent. Additionally, the contents of 5-hydroxymethylfurfural (HMF), as high-value product, were determined in the liquid products obtained from HTC processing, as well as in the condensate obtained after WT processing. Specific surface areas of the activated hydrochars may still be too low for application as adsorbent material. Hence, its use as a biofertilizer and soil improver should be preferred. Interestingly, the liquid fraction obtained from the innovative WT process displayed a significantly higher 5-HMF content compared to the conventional HTC process. |
|---|