Corrosion resistance and bioactivity enhancement of MAO coated Mg alloy depending on the time of hydrothermal treatment in Ca-EDTA solution
Abstract In this study, a two-step surface treatment was developed to restrain the rapid primary degradation of a biodegradable Mg alloy and to improve their biocompatibility. Micro arc oxidation (MAO) coating was performed in alkaline electrolytes such as 1.0 M NaOH with 0.1 M glycerol and 0.1 M Na...
Guardado en:
| Autores principales: | , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Nature Portfolio
2017
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/1e6c39df85f346268d30ecf2a994f597 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Abstract In this study, a two-step surface treatment was developed to restrain the rapid primary degradation of a biodegradable Mg alloy and to improve their biocompatibility. Micro arc oxidation (MAO) coating was performed in alkaline electrolytes such as 1.0 M NaOH with 0.1 M glycerol and 0.1 M Na3PO4. Hydrothermal treatment was performed in 0.1 M Ca-EDTA (C10H12CaN2Na2O8) and 0.5 M NaOH solution at 90 °C for different times (6, 12, 24, and 48 h). The film morphology and chemical properties were evaluated by XRD and FE-SEM. The electrochemical and corrosion behaviors were examined in the simulated body fluid, and cytotoxicity was assessed using MC3T3-E1 cells. After MAO coating, an oxide layer containing $${\bf{P}}{{\bf{O}}}_{4}^{3-}$$ P O 4 3 − formed on the surface. During the hydrothermal treatment in Ca-EDTA solution, calcium phosphate and Mg(OH)2 were produced via a reaction between $${\bf{P}}{{\bf{O}}}_{4}^{3-}$$ P O 4 3 − on the surface and Ca2+ in solution. The layer with ceramics and oxides was grown on the surface with increasing hydrothermal treatment time, and improved the surface corrosion resistance. The 24 h hydrothermal-treated group showed the lowest immersion corrosion rate and high cell viability. Therefore, this treatment was the most favorable surface modification for improving the initial corrosion resistance and bioactivity of the biodegradable Mg alloy. |
|---|