Influence of nano-VC on the structural and magnetic properties of MnAlC-alloy
Abstract Alloys of Mn55Al45C2 with additions of VC nano-particles have been synthesized and their properties evaluated. The Mn55Al45C2(VC) x (x = 0.25, 0.5 and 1) alloys have been prepared by induction melting resulting in a high content of the ferromagnetic τ-phase (> 94 wt.%). Powder X-ray diff...
Guardado en:
| Autores principales: | , , , , , , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Nature Portfolio
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/21d877175fb54cccab064bc0c2423157 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Abstract Alloys of Mn55Al45C2 with additions of VC nano-particles have been synthesized and their properties evaluated. The Mn55Al45C2(VC) x (x = 0.25, 0.5 and 1) alloys have been prepared by induction melting resulting in a high content of the ferromagnetic τ-phase (> 94 wt.%). Powder X-ray diffraction indicates that nano-VC can be dissolved in the alloy matrix up to 1 at.%. On the other side, metallography investigations by scanning electron microscopy and scanning transmission electron microscope show inclusions of the nanosized additives in the microstructure. The effect of nano-VC on the grain and twin boundaries has been studied by electron backscattering diffraction. The magnetization has been measured by magnetometry up to 9 T while the domain structure has been studied using both magnetic force microscopy as well as Kerr-microscopy. For nano-VC contents above 0.25 at.%, a clear increase of the coercive force is observed, from 57 to 71 kA/m. The optimum appears to be for 0.5 at.% nano-VC which shows a 25% increase in coercive force without losing any saturation magnetization. This independent increase in coercivity is believed to originate from the nano-VC reducing the overall magnetic domain size. Overall, we observe that addition of nano-VC could be an interesting route to increase the coercive force of MnAl, without sacrificing saturation magnetization. |
|---|