Microstructures, mechanical behavior and strengthening mechanism of TiSiCN nanocomposite films

Abstract Currently, the arguments have existed in the strengthening mechanism and microstructural model of the nanocomposite film due to lack of the convincible experimental evidences. In this investigation, the quarternary TiSiCN nanocomposite films with the different C and Si contents are synthesi...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Wei Li, Ping Liu, Zenghui Xue, Fengcang Ma, Ke Zhang, Xiaohong Chen, Rui Feng, Peter K. Liaw
Formato: article
Lenguaje:EN
Publicado: Nature Portfolio 2017
Materias:
R
Q
Acceso en línea:https://doaj.org/article/261ef31fe79a40f6b904806677ef6238
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
Descripción
Sumario:Abstract Currently, the arguments have existed in the strengthening mechanism and microstructural model of the nanocomposite film due to lack of the convincible experimental evidences. In this investigation, the quarternary TiSiCN nanocomposite films with the different C and Si contents are synthesized by the reactive-magnetron-sputtering technique. The TiSiCN film is characterized as the nanocomposite structure with the TiN nanocrystallites surrounded by the (Si3N4 + C + CNx) interface phase. When the C/Si content ratio is 2:2, the TiSiCN nanocomposite film is remarkably strengthened with the maximal hardness and elastic modulus of 46.1 GPa and 425 GPa, respectively. Meanwhile, the (Si3N4 + C + CNx) interfaces exhibit as a crystallized form, which can coordinate the growth misorientations and maintain the coherently epitaxial growth between the TiN nanocrystallites and interfaces. Through the high-resolution transmission electron microscopy (HRTEM) observations, this investigation firstly provides the direct experimental evidence for the crystallized feature of the interfaces when the TiSiCN nanocomposite film is strengthened, suggesting that the strengthening effect of the TiSiCN nanocomposite film can be attributed to the coherent-interface strengthening mechanism, which is expressed as the “nc-TiN/c-Si3N4/c-C/c-CNx” model.