Alumina-Forming Austenitic (AFA) steels and aluminium-based coating on 15-15 Ti steel to limit mechanical damage in presence of liquid lead-bismuth eutectic and liquid lead
To limit corrosion of the steels in contact with liquid metal (Pb or Pb-Bi), both different solutions based on the presence of alumina at the surface of the steels were selected: 2 Alumina-Forming Austenitic (AFA) steels and the 15-15 Ti steel coated by alumina layer. These technical options to miti...
Guardado en:
Autores principales: | Proriol Serre Ingrid, Ponsot Ines, Vogt Jean-Bernard |
---|---|
Formato: | article |
Lenguaje: | EN FR |
Publicado: |
EDP Sciences
2021
|
Materias: | |
Acceso en línea: | https://doaj.org/article/26dd6ba3b54a4824b63e204f71f06b5e |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares
-
Characteristics of iron and nickel diffusion in molten lead-bismuth eutectic
por: Yun GAO, et al.
Publicado: (2015) -
Cryogenic toughness in a low-cost austenitic steel
por: Yuhui Wang, et al.
Publicado: (2021) -
Effect of the Small Punch Test sample geometry on the Liquid Metal Embrittlement of Cu-30 wt% Zn by the eGaIn
por: Ezequiel Marco, et al.
Publicado: (2021) -
Quantitative Estimation of Adsorbed Water Layer on Austenitic Stainless Steel
por: Zaid Ali Subhi, et al.
Publicado: (2015) -
Influence of C and N on Strain-Induced Martensite Formation in Fe-15Cr-7Mn-4Ni-0.5Si Austenitic Steel
por: Caroline Quitzke, et al.
Publicado: (2021)