Formability and Magnetic Properties of the Binary Nd-Co Amorphous Alloys
In this paper, binary Nd-Co alloys with compositional range from Nd<sub>72.5</sub>Co<sub>27.5</sub> to Nd<sub>50</sub>Co<sub>50</sub> were successfully vitrified into glassy state by a melt-spinning method. The glass formability of the metallic glasses...
Guardado en:
| Autores principales: | , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
MDPI AG
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/281b1a225df4464191ff50a348081944 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | In this paper, binary Nd-Co alloys with compositional range from Nd<sub>72.5</sub>Co<sub>27.5</sub> to Nd<sub>50</sub>Co<sub>50</sub> were successfully vitrified into glassy state by a melt-spinning method. The glass formability of the metallic glasses (MGs) was studied and the best glass former in the binary Nd-Co alloys was obtained. Magnetic properties of the MGs were measured. The compositional dependence of Curie temperature of the MGs was observed. The mechanism for the spin-glass-like behaviors and high coercivity at low temperature, and their influence on the magnetic entropy change of the MGs, were investigated. |
|---|