Polyacrylonitrile nanofibers coated with silver nanoparticles using a modified coaxial electrospinning process
Deng-Guang Yu,1 Jie Zhou,2 Nicholas P Chatterton,3 Ying Li,1 Jing Huang,2 Xia Wang11School of Materials Science and Engineering, University of Shanghai for Science and Technology, Shanghai, People's Republic of China; 2School of Life Sciences, East China Normal University, Shanghai, Peop...
Guardado en:
| Autores principales: | , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Dove Medical Press
2012
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/2c363650199842e2ba921771b9aaf040 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Deng-Guang Yu,1 Jie Zhou,2 Nicholas P Chatterton,3 Ying Li,1 Jing Huang,2 Xia Wang11School of Materials Science and Engineering, University of Shanghai for Science and Technology, Shanghai, People's Republic of China; 2School of Life Sciences, East China Normal University, Shanghai, People's Republic of China; 3Faculty of Life Sciences, London Metropolitan University, London, United KingdomBackground: The objective of this investigation was to develop a new class of antibacterial material in the form of nanofibers coated with silver nanoparticles (AgNPs) using a modified coaxial electrospinning approach. Through manipulation of the distribution on the surface of nanofibers, the antibacterial effect of Ag can be improved substantially.Methods: Using polyacrylonitrile (PAN) as the filament-forming polymer matrix, an electrospinnable PAN solution was prepared as the core fluid. A silver nitrate (AgNO3) solution was exploited as sheath fluid to carry out the modified coaxial electrospinning process under varied sheath-to-core flow rate ratios.Results: Scanning electron microscopy and transmission electron microscopy demonstrated that the sheath AgNO3 solution can take a role in reducing the nanofibers' diameters significantly, a sheath-to-core flow rate ratio of 0.1 and 0.2 resulting in PAN nanofibers with diameters of 380 ± 110 nm and 230 ± 70 nm respectively. AgNPs are well distributed on the surface of PAN nanofibers. The antibacterial experiments demonstrated that these nanofibers show strong antimicrobial activities against Bacillus subtilis Wb800, and Escherichia coli dh5α.Conclusion: Coaxial electrospinning with AgNO3 solution as sheath fluid not only facilitates the electrospinning process, providing nanofibers with reduced diameters, but also allows functionalization of the nanofibers through coating with functional ingredients, effectively ensuring that the active antibacterial component is on the surface of the material, which leads to enhanced activity. We report an example of the systematic design, preparation, and application of a novel type of antibacterial material coated with AgNPs via a modified coaxial electrospinning methodology.Keywords: antibacteria, nanofibers, nano-coating, coaxial electrospinning, Ag nanoparticles |
|---|