Effect of the Partial Substitution of Zn with Co, Ni, and Co-Ni on Microstructures and Mechanical Properties of Long-Period Stacking Ordered Dominant Mg-Y-Zn Alloys
The microstructures of Mg96Y2Zn2, Mg96Y2Zn1Co1, Mg96Y2Zn1Ni1, and Mg96Y2Zn1Co0.5Ni0.5 (at.%) alloys were investigated by XRD, SEM/EDS, and TEM. The α-Mg matrix, the long-period stacking ordered (LPSO) phase, and the bright compounds were observed in the as-cast alloys. The ability of Co to form LPSO...
Guardado en:
Autores principales: | , , , , , |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
Hindawi Limited
2021
|
Materias: | |
Acceso en línea: | https://doaj.org/article/334dcad7b7394729ae6e543e46740fbc |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
id |
oai:doaj.org-article:334dcad7b7394729ae6e543e46740fbc |
---|---|
record_format |
dspace |
spelling |
oai:doaj.org-article:334dcad7b7394729ae6e543e46740fbc2021-11-08T02:36:37ZEffect of the Partial Substitution of Zn with Co, Ni, and Co-Ni on Microstructures and Mechanical Properties of Long-Period Stacking Ordered Dominant Mg-Y-Zn Alloys1687-844210.1155/2021/8922503https://doaj.org/article/334dcad7b7394729ae6e543e46740fbc2021-01-01T00:00:00Zhttp://dx.doi.org/10.1155/2021/8922503https://doaj.org/toc/1687-8442The microstructures of Mg96Y2Zn2, Mg96Y2Zn1Co1, Mg96Y2Zn1Ni1, and Mg96Y2Zn1Co0.5Ni0.5 (at.%) alloys were investigated by XRD, SEM/EDS, and TEM. The α-Mg matrix, the long-period stacking ordered (LPSO) phase, and the bright compounds were observed in the as-cast alloys. The ability of Co to form LPSO phase with Mg and Y is weaker than that of Zn, but it can produce some new intermetallic compounds. The effect of Ni on phase content of alloys was opposite to that of Co. After replacing partial Zn with Co and Ni, the increase in the LPSO phase is more obvious than that of Co or Ni alone to replace partial Zn. The ability to form LPSO phase with Mg and Y atoms in Mg-Y-TM alloys can be ranked as follows: Co-Ni > Ni > Zn > Co. From the point-of-view of mechanical performance, the substitution of Co-Ni for partial replacement of Zn exhibited the best yield strength; the tensile yield strength, ultimate tensile strength, compressive yield stress, and ultimate compressive stress of which were 345 MPa, 453 MPa, 335 MPa, and 470 MPa, respectively. However, the ductility did not improve significantly.Heng XueJinbei LyuFengxue WangHongxin LiaoJonghyun KimFusheng PanHindawi LimitedarticleMaterials of engineering and construction. Mechanics of materialsTA401-492ENAdvances in Materials Science and Engineering, Vol 2021 (2021) |
institution |
DOAJ |
collection |
DOAJ |
language |
EN |
topic |
Materials of engineering and construction. Mechanics of materials TA401-492 |
spellingShingle |
Materials of engineering and construction. Mechanics of materials TA401-492 Heng Xue Jinbei Lyu Fengxue Wang Hongxin Liao Jonghyun Kim Fusheng Pan Effect of the Partial Substitution of Zn with Co, Ni, and Co-Ni on Microstructures and Mechanical Properties of Long-Period Stacking Ordered Dominant Mg-Y-Zn Alloys |
description |
The microstructures of Mg96Y2Zn2, Mg96Y2Zn1Co1, Mg96Y2Zn1Ni1, and Mg96Y2Zn1Co0.5Ni0.5 (at.%) alloys were investigated by XRD, SEM/EDS, and TEM. The α-Mg matrix, the long-period stacking ordered (LPSO) phase, and the bright compounds were observed in the as-cast alloys. The ability of Co to form LPSO phase with Mg and Y is weaker than that of Zn, but it can produce some new intermetallic compounds. The effect of Ni on phase content of alloys was opposite to that of Co. After replacing partial Zn with Co and Ni, the increase in the LPSO phase is more obvious than that of Co or Ni alone to replace partial Zn. The ability to form LPSO phase with Mg and Y atoms in Mg-Y-TM alloys can be ranked as follows: Co-Ni > Ni > Zn > Co. From the point-of-view of mechanical performance, the substitution of Co-Ni for partial replacement of Zn exhibited the best yield strength; the tensile yield strength, ultimate tensile strength, compressive yield stress, and ultimate compressive stress of which were 345 MPa, 453 MPa, 335 MPa, and 470 MPa, respectively. However, the ductility did not improve significantly. |
format |
article |
author |
Heng Xue Jinbei Lyu Fengxue Wang Hongxin Liao Jonghyun Kim Fusheng Pan |
author_facet |
Heng Xue Jinbei Lyu Fengxue Wang Hongxin Liao Jonghyun Kim Fusheng Pan |
author_sort |
Heng Xue |
title |
Effect of the Partial Substitution of Zn with Co, Ni, and Co-Ni on Microstructures and Mechanical Properties of Long-Period Stacking Ordered Dominant Mg-Y-Zn Alloys |
title_short |
Effect of the Partial Substitution of Zn with Co, Ni, and Co-Ni on Microstructures and Mechanical Properties of Long-Period Stacking Ordered Dominant Mg-Y-Zn Alloys |
title_full |
Effect of the Partial Substitution of Zn with Co, Ni, and Co-Ni on Microstructures and Mechanical Properties of Long-Period Stacking Ordered Dominant Mg-Y-Zn Alloys |
title_fullStr |
Effect of the Partial Substitution of Zn with Co, Ni, and Co-Ni on Microstructures and Mechanical Properties of Long-Period Stacking Ordered Dominant Mg-Y-Zn Alloys |
title_full_unstemmed |
Effect of the Partial Substitution of Zn with Co, Ni, and Co-Ni on Microstructures and Mechanical Properties of Long-Period Stacking Ordered Dominant Mg-Y-Zn Alloys |
title_sort |
effect of the partial substitution of zn with co, ni, and co-ni on microstructures and mechanical properties of long-period stacking ordered dominant mg-y-zn alloys |
publisher |
Hindawi Limited |
publishDate |
2021 |
url |
https://doaj.org/article/334dcad7b7394729ae6e543e46740fbc |
work_keys_str_mv |
AT hengxue effectofthepartialsubstitutionofznwithconiandconionmicrostructuresandmechanicalpropertiesoflongperiodstackingordereddominantmgyznalloys AT jinbeilyu effectofthepartialsubstitutionofznwithconiandconionmicrostructuresandmechanicalpropertiesoflongperiodstackingordereddominantmgyznalloys AT fengxuewang effectofthepartialsubstitutionofznwithconiandconionmicrostructuresandmechanicalpropertiesoflongperiodstackingordereddominantmgyznalloys AT hongxinliao effectofthepartialsubstitutionofznwithconiandconionmicrostructuresandmechanicalpropertiesoflongperiodstackingordereddominantmgyznalloys AT jonghyunkim effectofthepartialsubstitutionofznwithconiandconionmicrostructuresandmechanicalpropertiesoflongperiodstackingordereddominantmgyznalloys AT fushengpan effectofthepartialsubstitutionofznwithconiandconionmicrostructuresandmechanicalpropertiesoflongperiodstackingordereddominantmgyznalloys |
_version_ |
1718443079725219840 |