Three-point bending test of laminated glass with PVB and EVA interlayers at elevated temperature

This paper presents the experimental results of a three-point bending test conducted on laminated glass at elevated temperature in an environmental chamber. The focus of the present research was on bending stiffness degradation of the laminated glass in correspondence to elevated temperature. The t...

Description complète

Enregistré dans:

Détails bibliographiques
Auteur principal:	David Antolinc
Format:	article
Langue:	EN
Publié:	Challenging Glass Conference 2020
Sujets:	Laminated glass, interlayer, bending stiffness, elevated temperature, failure mode Clay industries. Ceramics. Glass TP785-869
Accès en ligne:	https://doaj.org/article/3f569ee84003405f928dbe07a347c99a
Tags:	Ajouter un tag Pas de tags, Soyez le premier à ajouter un tag!

id	oai:doaj.org-article:3f569ee84003405f928dbe07a347c99a
record_format	dspace
spelling	oai:doaj.org-article:3f569ee84003405f928dbe07a347c99a2021-12-04T05:11:38ZThree-point bending test of laminated glass with PVB and EVA interlayers at elevated temperature10.7480/cgc.7.44912589-8019https://doaj.org/article/3f569ee84003405f928dbe07a347c99a2020-09-01T00:00:00Zhttps://proceedings.challengingglass.com/index.php/cgc/article/view/318https://doaj.org/toc/2589-8019 This paper presents the experimental results of a three-point bending test conducted on laminated glass at elevated temperature in an environmental chamber. The focus of the present research was on bending stiffness degradation of the laminated glass in correspondence to elevated temperature. The tested specimens were made of two fully tempered glass plates bonded with EVA and PVB interlayers. For each type of laminated glass and set temperature, we prepared and tested 5 specimens. Each of the specimen was preconditioned to a set temperature before the experiment conducted in an environmental chamber. The tests were conducted at 23°C, 35°C and 60°C after the specimens had reached the defined contact temperature. During the experiment, the midspan deflection, longitudinal midspan deformation and the force at midspan were recorded. In the end, the behaviour of two different types of laminated glass plates was compared based on measured midspan deflection, deformations and stiffness degradation. Based on the results it can be seen that the laminated glass with EVA interlayer behaves stiffer and that the stiffness degradation is almost linear and slower in comparison to the specimens with PVB interlayer. David AntolincChallenging Glass ConferencearticleLaminated glass, interlayer, bending stiffness, elevated temperature, failure modeClay industries. Ceramics. GlassTP785-869ENChallenging Glass Conference Proceedings, Vol 7, Iss 1 (2020)
institution	DOAJ
collection	DOAJ
language	EN
topic	Laminated glass, interlayer, bending stiffness, elevated temperature, failure mode Clay industries. Ceramics. Glass TP785-869
spellingShingle	Laminated glass, interlayer, bending stiffness, elevated temperature, failure mode Clay industries. Ceramics. Glass TP785-869 David Antolinc Three-point bending test of laminated glass with PVB and EVA interlayers at elevated temperature
description	This paper presents the experimental results of a three-point bending test conducted on laminated glass at elevated temperature in an environmental chamber. The focus of the present research was on bending stiffness degradation of the laminated glass in correspondence to elevated temperature. The tested specimens were made of two fully tempered glass plates bonded with EVA and PVB interlayers. For each type of laminated glass and set temperature, we prepared and tested 5 specimens. Each of the specimen was preconditioned to a set temperature before the experiment conducted in an environmental chamber. The tests were conducted at 23°C, 35°C and 60°C after the specimens had reached the defined contact temperature. During the experiment, the midspan deflection, longitudinal midspan deformation and the force at midspan were recorded. In the end, the behaviour of two different types of laminated glass plates was compared based on measured midspan deflection, deformations and stiffness degradation. Based on the results it can be seen that the laminated glass with EVA interlayer behaves stiffer and that the stiffness degradation is almost linear and slower in comparison to the specimens with PVB interlayer.
format	article
author	David Antolinc
author_facet	David Antolinc
author_sort	David Antolinc
title	Three-point bending test of laminated glass with PVB and EVA interlayers at elevated temperature
title_short	Three-point bending test of laminated glass with PVB and EVA interlayers at elevated temperature
title_full	Three-point bending test of laminated glass with PVB and EVA interlayers at elevated temperature
title_fullStr	Three-point bending test of laminated glass with PVB and EVA interlayers at elevated temperature
title_full_unstemmed	Three-point bending test of laminated glass with PVB and EVA interlayers at elevated temperature
title_sort	three-point bending test of laminated glass with pvb and eva interlayers at elevated temperature
publisher	Challenging Glass Conference
publishDate	2020
url	https://doaj.org/article/3f569ee84003405f928dbe07a347c99a
work_keys_str_mv	AT davidantolinc threepointbendingtestoflaminatedglasswithpvbandevainterlayersatelevatedtemperature
_version_	1718372848060334080

Three-point bending test of laminated glass with PVB and EVA interlayers at elevated temperature

Documents similaires