Super fine cerium hydroxide abrasives for SiO2 film chemical mechanical planarization performing scratch free
Abstract Face-centered-cubic crystallized super-fine (~ 2 nm in size) wet-ceria-abrasives are synthesized using a novel wet precipitation process that comprises a Ce4+ precursor, C3H4N2 catalyst, and NaOH titrant for a synthesized termination process at temperature of at temperature of 25 °C. This p...
Guardado en:
| Autores principales: | , , , , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Nature Portfolio
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/3fb08806d82440e48508ac56b10314b3 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Abstract Face-centered-cubic crystallized super-fine (~ 2 nm in size) wet-ceria-abrasives are synthesized using a novel wet precipitation process that comprises a Ce4+ precursor, C3H4N2 catalyst, and NaOH titrant for a synthesized termination process at temperature of at temperature of 25 °C. This process overcomes the limitations of chemical–mechanical-planarization (CMP)-induced scratches from conventional dry ceria abrasives with irregular surfaces or wet ceria abrasives with crystalline facets in nanoscale semiconductor devices. The chemical composition of super-fine wet ceria abrasives depends on the synthesis termination pH, that is, Ce(OH)4 abrasives at a pH of 4.0–5.0 and a mixture of CeO2 and Ce(OH)4 abrasives at a pH of 5.5–6.5. The Ce(OH)4 abrasives demonstrate better abrasive stability in the SiO2-film CMP slurry than the CeO2 abrasives and produce a minimum abrasive zeta potential (~ 12 mV) and a minimum secondary abrasive size (~ 130 nm) at the synthesis termination pH of 5.0. Additionally, the abrasive stability of the SiO2-film CMP slurry that includes super-fine wet ceria abrasives is notably sensitive to the CMP slurry pH; the best abrasive stability (i.e., a minimum secondary abrasive size of ~ 130 nm) is observed at a specific pH (6.0). As a result, a maximum SiO2-film polishing rate (~ 524 nm/min) is achieved at pH 6.0, and the surface is free of stick-and-slip type scratches. |
|---|