INVESTIGATION ON POSSIBILITY OF MDF PRODUCTION FROM REED
In this study, MDF was produced from Reed (Phragmites australis). Reeds are collected from Hor-Alazym area. The treatments conditions for fiber preparing were as following:- Steaming temperature 170, 180oC(Steaming pressure 7,9 bar).- Steaming time 5, 10, 15 minutes.The other production variables we...
Guardado en:
| Autores principales: | , , , |
|---|---|
| Formato: | article |
| Lenguaje: | FA |
| Publicado: |
Regional Information Center for Science and Technology (RICeST)
2004
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/415768f15a5942f091e54538341f0a7b |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | In this study, MDF was produced from Reed (Phragmites australis). Reeds are collected from Hor-Alazym area. The treatments conditions for fiber preparing were as following:- Steaming temperature 170, 180oC(Steaming pressure 7,9 bar).- Steaming time 5, 10, 15 minutes.The other production variables were constant.The anatomical properties of Reed such as Fiber length, fiber diameter, lumen cell diameter, and cell wall thickness were measured. LID ratio of Reed fiber was measured 73.69. The physical and mechanical properties of MDF were determined according to DIN standard. The measurements of bending properties and IB of MDF revealed that increasing steaming time and steaming temperature caused to decrease MOR, MOE, and IB.Also the results of MDF dimentional stabilities indicated that Thickness Swelling after 2 and 24 hours decreased upon increasing steaming time and steaming temperature. Degradation of hemicellulose chains may be the reason of decreasing Thickness Swelling. |
|---|