Nonlinear optical property measurements of rhenium diselenide used for ultrafast fiber laser mode-locking at 1.9 μm
Abstract An experimental investigation into the nonlinear optical properties of rhenium diselenide (ReSe2) was conducted at a wavelength of 1.9 μm using the open-aperture and closed-aperture Z-scan techniques for the nonlinear optical coefficient (β) and nonlinear refractive index (n 2) of ReSe2, re...
Guardado en:
| Autores principales: | , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Nature Portfolio
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/41b05bc72a024019bb13f44d5ce0e4ce |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Abstract An experimental investigation into the nonlinear optical properties of rhenium diselenide (ReSe2) was conducted at a wavelength of 1.9 μm using the open-aperture and closed-aperture Z-scan techniques for the nonlinear optical coefficient (β) and nonlinear refractive index (n 2) of ReSe2, respectively. β and n 2 measured at 1.9 μm were ~ − 11.3 × 103 cm/GW and ~ − 6.2 × 10–2 cm2/GW, respectively, which to the best of our knowledge, are the first reported measurements for ReSe2 in the 1.9-μm spectral region. The electronic band structures of both ReSe2 and its defective structures were also calculated via the Perdew–Becke–Erzenhof functional to better understand their absorption properties. A saturable absorber (SA) was subsequently fabricated to demonstrate the usefulness of ReSe2 for implementing a practical nonlinear optical device at 1.9 μm. The 1.9-μm SA exhibited a modulation depth of ~ 8% and saturation intensity of ~ 11.4 MW/cm2. The successful use of the ReSe2-based SA for mode-locking of a thulium–holmium (Tm–Ho) co-doped fiber ring cavity was achieved with output pulses of ~ 840 fs at 1927 nm. We believe that the mode-locking was achieved through a hybrid mechanism of saturable absorption and nonlinear polarization rotation. |
|---|