Quasi-static and high strain rate response of Kevlar reinforced thermoplastics
The present study deals with the quasi-static and high strain rate characterization of Kevlar-129 based thermoplastic composites. Two different thermoplastic matrices, namely, Polypropylene (PP) and Polyetherimide (PEI) were used to manufacture composite laminates. Quasi-static compression tests wer...
Guardado en:
| Autores principales: | , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Elsevier
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/4263441a5ca74c25aa45725085892987 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | The present study deals with the quasi-static and high strain rate characterization of Kevlar-129 based thermoplastic composites. Two different thermoplastic matrices, namely, Polypropylene (PP) and Polyetherimide (PEI) were used to manufacture composite laminates. Quasi-static compression tests were performed at strain rates of 0.041 s−1 and 0.045 s−1. High strain rate tests were performed using a split Hopkinson pressure bar apparatus within the strain rates ranging from 2548 s−1 to 4379 s−1. Stress-strain relations reveals the rate-sensitive behaviour of composites. Kevlar/PP (K-PP) showed higher peak stress under quasi-static loading as compared to the high strain rate test. Comparable peak stresses were revealed under quasi-static and high strain rate loading for Kevlar/PEI (K-PEI) composite. Also, high strain rate compression properties such as peak stress, peak strain and toughness of K-PP were 25%, 27% and 6% higher than that of the K-PEI composite. The failure mechanisms of both the composites were characterized through macroscopic and scanning electron microscopy. K-PP failed majorly due to matrix crush and fibre failure while K-PEI failed due to shear cracking. Damage study reveals that a single fibre based composite system can be tailored to act as an energy-absorbing or dissipating material system by varying the thermoplastic matrix materials. |
|---|