Correlating work hardening with co-activation of stacking fault strengthening and transformation in a high entropy alloy using in-situ neutron diffraction
Abstract Transformation induced plasticity (TRIP) leads to enhancements in ductility in low stacking fault energy (SFE) alloys, however to achieve an unconventional increase in strength simultaneously, there must be barriers to dislocation motion. While stacking faults (SFs) contribute to strengthen...
Guardado en:
Autores principales: | M. Frank, S. S. Nene, Y. Chen, B. Gwalani, E. J. Kautz, A. Devaraj, K. An, R. S. Mishra |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
Nature Portfolio
2020
|
Materias: | |
Acceso en línea: | https://doaj.org/article/42a2604f811848f9861b9980a5debd2c |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares
-
Stacking Fault Energy Analyses of Additively Manufactured Stainless Steel 316L and CrCoNi Medium Entropy Alloy Using In Situ Neutron Diffraction
por: W. Woo, et al.
Publicado: (2020) -
Co-introduction of precipitate hardening and TRIP in a TWIP high-entropy alloy using friction stir alloying
por: Tianhao Wang, et al.
Publicado: (2021) -
Extremely high strength and work hardening ability in a metastable high entropy alloy
por: S. S. Nene, et al.
Publicado: (2018) -
Hardening in Au-Ag nanoboxes from stacking fault-dislocation interactions
por: Radhika P. Patil, et al.
Publicado: (2020) -
Stacking fault energy in concentrated alloys
por: Mulaine Shih, et al.
Publicado: (2021)