Synthesis, characterization and catalytic testing of MCM-22 derived catalysts for n-hexane cracking
Abstract Layered zeolites and their delaminated structures are novel materials that enhance the catalytic performance of catalysts by addressing diffusion limitations of the reactant molecules. n-Hexane catalytic cracking was observed over MCM-22 layered zeolite and its derivative structures over th...
Guardado en:
| Autores principales: | , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Nature Portfolio
2020
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/472e278652fa49fa9f184f16cf2711d9 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Abstract Layered zeolites and their delaminated structures are novel materials that enhance the catalytic performance of catalysts by addressing diffusion limitations of the reactant molecules. n-Hexane catalytic cracking was observed over MCM-22 layered zeolite and its derivative structures over the temperature range of 450–650 °C for the production of olefins. MCM-22, H-MCM-22, and ITQ-2 zeolites were prepared by the hydrothermal method. Oxalic acid was used as a dealuminating reagent to obtain H-MCM-22 with various Si/Al ratios ranging from 09–65. The prepared samples were characterized by XRD, SEM, TGA, and BET. The cracking of n-hexane was carried out by Pyro/GC–MS. It was observed that the selectivity for olefins was improved by increasing the Si/Al ratio. H-MCM-22–10% produced the highest relative olefinic concentration of 68% as compared to other dealuminated structures. Moreover, the product distribution showed that higher reaction temperature is favorable to produce more olefins. Furthermore, a comparison between ITQ-2 and MCM-22 derived structures showed that ITQ-2 is more favorable for olefins production at high temperatures. The concentration of relative olefins was increased up to 80% over ITQ-2 at 650 °C. |
|---|