Sacrificial gold coating enhances transport of liquid metal in pressurized fountain pen lithography
Abstract Liquid metals have attracted attention as functional components for moldable electronics, such as soft flexible connectors, wires or conductive ink. The relatively high surface tension (> 400 mN m−1) and the fact that liquid metals do not readily wet ceramic or oxide surfaces have led to...
Guardado en:
| Autores principales: | , , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Nature Portfolio
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/473ac4768b3d4b4da017a742de091294 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Abstract Liquid metals have attracted attention as functional components for moldable electronics, such as soft flexible connectors, wires or conductive ink. The relatively high surface tension (> 400 mN m−1) and the fact that liquid metals do not readily wet ceramic or oxide surfaces have led to devising unique techniques to spread the liquid and mold its shape. These techniques include surface modification, electrowetting and vacuum filling of channels. This work presents an injection technique based on pressurized fountain pen lithography with glass nanopipettes developed to directly pattern liquid metal on flat hard substrates. The liquid metals were eutectic alloys of Gallium, including Gallium-Indium (EGaIn), Gallium-Indium-Zinc and Gallium-Indium-Tin. The nanopipettes were coated internally with gold, acting as a sacrificial layer and facilitating the wetting of the pipette down to its pore, with an inner diameter of ~ 100–300 nm. By applying hydrodynamic pressure to the connected end of the pipette, the metal was extruded through the pore, forming long continuous (> 3 mm) and narrow (~ 1–15 µm) metal lines on silicon oxide and gold surfaces at room temperature and ambient conditions. With this robust platform, it is possible to pattern liquid metals on a variety of substrates and geometries down to the micron range. |
|---|