Effects of Ni doping on various properties of NbH phases: A first-principles investigation

Abstract Changes in the stability, hydrogen diffusion, and mechanical properties of the NbH phases from Ni-doping was studied by using first-principles methods. The calculation results reveal that the single H atom adsorption is energetically favorable at the tetrahedral interstitial site (TIS) and...

Full description

Saved in:
Bibliographic Details
Main Authors: Yang Wu, Zhongmin Wang, Dianhui Wang, Zhenzhen Wan, Yan Zhong, Chaohao Hu, Huaiying Zhou
Format: article
Language:EN
Published: Nature Portfolio 2017
Subjects:
R
Q
Online Access:https://doaj.org/article/4a1df6a36d30498595fd2d30bbec5f11
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Abstract Changes in the stability, hydrogen diffusion, and mechanical properties of the NbH phases from Ni-doping was studied by using first-principles methods. The calculation results reveal that the single H atom adsorption is energetically favorable at the tetrahedral interstitial site (TIS) and octahedral interstitial site (OIS). The preferred path of H diffusion is TIS-to-TIS, followed by TIS-to-OIS in both Nb16H and Nb15NiH. Ni-doping in the Nb15NiH alloy lowers the energy barrier of H diffusion, enhances the H-diffusion coefficient (D) and mechanical properties of the Nb16H phase. The value of D increases with increasing temperature, and this trend due to Ni doping clearly becomes weaker at higher temperatures. At the typical operating temperature of 400 K, the D value of Nb15NiH (TIS) is about 1.90 × 10−8 m2/s, which is about 80 times higher than that of Nb16H (TIS) (2.15 × 10−10 m2/s). Our calculations indicated that Ni-doping can greatly improve the diffusion of H in Nb.