Fabrication of Carbon Nanotube Reinforced Al2O3/Cr2O3 Nanocomposites by Coprecipitation Process

In this research, the effect of multi-walled carbon nanotubes (MWCNTs) on the alumina/chromia (Al2O3/Cr2O3) nanocomposites has been investigated. Al2O3/Cr2O3-MWCNTs nanocomposites with variable contents of Cr2O3 and MWCNTs were fabricated using coprecipitation process and followed by spark plasma s...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autor principal: Hussein Alaa Jaber
Formato: article
Lenguaje:EN
Publicado: Al-Khwarizmi College of Engineering – University of Baghdad 2017
Materias:
Acceso en línea:https://doaj.org/article/4a5a1f641d1942e0b2fdbc1ef7fe1778
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
Descripción
Sumario:In this research, the effect of multi-walled carbon nanotubes (MWCNTs) on the alumina/chromia (Al2O3/Cr2O3) nanocomposites has been investigated. Al2O3/Cr2O3-MWCNTs nanocomposites with variable contents of Cr2O3 and MWCNTs were fabricated using coprecipitation process and followed by spark plasma sintering. XRD analysis revealed a good crystallinity of sintered nanocomposites samples and there was only one phase presence of Al2O3-Cr2O3 solid solution. Density, Vickers microhardness, fracture toughness and fracture strength have been measured in the sintered samples. The results show that the relative density, microhardness and fracture strength of nanocomposites are significantly improved at low contents of Cr2O3 and MWCNTs. The increase of MWCNT’s content in the nanocomposites has adversely affected due to increasing the tangle and interaction of MWCNTs with each other, which leads to agglomeration in the nanocomposites. Increasing of Cr2O3 content in nanocomposites increases formation of Al2O3-Cr2O3 solid solution that actually requires the high sintering temperature to achieve good densification. The fracture toughness of Al2O3/Cr2O3-MWCNTs nanocomposites was enhanced by increasing the carbon nanotube content.