Functionalization of PLA aerogels with TiO2 nanoparticles
This study was aimed to prepare material with high porosity and photocatalytic activity by immobilization of TiO2 nanoparticles (NPs) onto poly(lactic acid) (PLA) aerogels. PLA aerogels were prepared in three steps: (1) dissolution of polymer in chloroform at 22 °C, (2) chloroform replacement with e...
Guardado en:
| Autores principales: | , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN SR |
| Publicado: |
Savez inženjera i tehničara Srbije
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/4d9d0134a3f84e80ac3c1d5482d8b349 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | This study was aimed to prepare material with high porosity and photocatalytic activity by immobilization of TiO2 nanoparticles (NPs) onto poly(lactic acid) (PLA) aerogels. PLA aerogels were prepared in three steps: (1) dissolution of polymer in chloroform at 22 °C, (2) chloroform replacement with ethanol, and (3) supercritical CO2-drying at pressure 19 MPa and temperature 39 ºC. Immobilization of TiO2 NPs was performed by in situ and ex situ methods. Obtained samples were characterized using SEM, EDX, and FTIR analysis. Photocatalytic activity of developed material was tested by following decolorization of dye C.I. Acid Orange 7 in water solution. It was shown that the morphology of PLA aerogels was slightly affected by TiO2 NPs immobilization. PLA aerogels with TiO2 NPs immobilized by ex situ method sustained floatability during test period and provided a complete decolorization of dye solution after 330 minutes of illumination. High photocatalytic activity of the sample was preserved within three repeated cycles of dye decolorization. |
|---|