Functionalization of PLA aerogels with TiO2 nanoparticles
This study was aimed to prepare material with high porosity and photocatalytic activity by immobilization of TiO2 nanoparticles (NPs) onto poly(lactic acid) (PLA) aerogels. PLA aerogels were prepared in three steps: (1) dissolution of polymer in chloroform at 22 °C, (2) chloroform replacement with e...
Guardado en:
Autores principales: | , , |
---|---|
Formato: | article |
Lenguaje: | EN SR |
Publicado: |
Savez inženjera i tehničara Srbije
2021
|
Materias: | |
Acceso en línea: | https://doaj.org/article/4d9d0134a3f84e80ac3c1d5482d8b349 |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
id |
oai:doaj.org-article:4d9d0134a3f84e80ac3c1d5482d8b349 |
---|---|
record_format |
dspace |
spelling |
oai:doaj.org-article:4d9d0134a3f84e80ac3c1d5482d8b3492021-12-05T21:39:59ZFunctionalization of PLA aerogels with TiO2 nanoparticles0040-21762560-308610.5937/tehnika2104403Mhttps://doaj.org/article/4d9d0134a3f84e80ac3c1d5482d8b3492021-01-01T00:00:00Zhttps://scindeks-clanci.ceon.rs/data/pdf/0040-2176/2021/0040-21762104403M.pdfhttps://doaj.org/toc/0040-2176https://doaj.org/toc/2560-3086This study was aimed to prepare material with high porosity and photocatalytic activity by immobilization of TiO2 nanoparticles (NPs) onto poly(lactic acid) (PLA) aerogels. PLA aerogels were prepared in three steps: (1) dissolution of polymer in chloroform at 22 °C, (2) chloroform replacement with ethanol, and (3) supercritical CO2-drying at pressure 19 MPa and temperature 39 ºC. Immobilization of TiO2 NPs was performed by in situ and ex situ methods. Obtained samples were characterized using SEM, EDX, and FTIR analysis. Photocatalytic activity of developed material was tested by following decolorization of dye C.I. Acid Orange 7 in water solution. It was shown that the morphology of PLA aerogels was slightly affected by TiO2 NPs immobilization. PLA aerogels with TiO2 NPs immobilized by ex situ method sustained floatability during test period and provided a complete decolorization of dye solution after 330 minutes of illumination. High photocatalytic activity of the sample was preserved within three repeated cycles of dye decolorization.Milovanović Stoja L.Marković Darka D.Nikolić Ivana D.Savez inženjera i tehničara Srbijearticlephotocatalytic activitypoly(lactic acid) aerogelsupercritical co2tio2 nanoparticlesEngineering (General). Civil engineering (General)TA1-2040ENSRTehnika, Vol 76, Iss 4, Pp 403-408 (2021) |
institution |
DOAJ |
collection |
DOAJ |
language |
EN SR |
topic |
photocatalytic activity poly(lactic acid) aerogel supercritical co2 tio2 nanoparticles Engineering (General). Civil engineering (General) TA1-2040 |
spellingShingle |
photocatalytic activity poly(lactic acid) aerogel supercritical co2 tio2 nanoparticles Engineering (General). Civil engineering (General) TA1-2040 Milovanović Stoja L. Marković Darka D. Nikolić Ivana D. Functionalization of PLA aerogels with TiO2 nanoparticles |
description |
This study was aimed to prepare material with high porosity and photocatalytic activity by immobilization of TiO2 nanoparticles (NPs) onto poly(lactic acid) (PLA) aerogels. PLA aerogels were prepared in three steps: (1) dissolution of polymer in chloroform at 22 °C, (2) chloroform replacement with ethanol, and (3) supercritical CO2-drying at pressure 19 MPa and temperature 39 ºC. Immobilization of TiO2 NPs was performed by in situ and ex situ methods. Obtained samples were characterized using SEM, EDX, and FTIR analysis. Photocatalytic activity of developed material was tested by following decolorization of dye C.I. Acid Orange 7 in water solution. It was shown that the morphology of PLA aerogels was slightly affected by TiO2 NPs immobilization. PLA aerogels with TiO2 NPs immobilized by ex situ method sustained floatability during test period and provided a complete decolorization of dye solution after 330 minutes of illumination. High photocatalytic activity of the sample was preserved within three repeated cycles of dye decolorization. |
format |
article |
author |
Milovanović Stoja L. Marković Darka D. Nikolić Ivana D. |
author_facet |
Milovanović Stoja L. Marković Darka D. Nikolić Ivana D. |
author_sort |
Milovanović Stoja L. |
title |
Functionalization of PLA aerogels with TiO2 nanoparticles |
title_short |
Functionalization of PLA aerogels with TiO2 nanoparticles |
title_full |
Functionalization of PLA aerogels with TiO2 nanoparticles |
title_fullStr |
Functionalization of PLA aerogels with TiO2 nanoparticles |
title_full_unstemmed |
Functionalization of PLA aerogels with TiO2 nanoparticles |
title_sort |
functionalization of pla aerogels with tio2 nanoparticles |
publisher |
Savez inženjera i tehničara Srbije |
publishDate |
2021 |
url |
https://doaj.org/article/4d9d0134a3f84e80ac3c1d5482d8b349 |
work_keys_str_mv |
AT milovanovicstojal functionalizationofplaaerogelswithtio2nanoparticles AT markovicdarkad functionalizationofplaaerogelswithtio2nanoparticles AT nikolicivanad functionalizationofplaaerogelswithtio2nanoparticles |
_version_ |
1718370941623336960 |