Temperature and preliminary deformation influence on micromechanical and acoustic-emission properties of MgO single crystals
The MgO single crystals were subjected to the annealing at Tan=150-600 °C as well as to the plastic deformation over ε=0-6% at 150 and 600 °C. The resting influence on the mechanical properties of these samples was investigated. It was established that with increasing of Tan and ε at Tdef
Guardado en:
| Autores principales: | , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
D.Ghitu Institute of Electronic Engineering and Nanotechnologies
2007
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/509002547a61450f9b85df1db4634b5e |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | The MgO single crystals were subjected to the annealing at Tan=150-600 °C as well as
to the plastic deformation over ε=0-6% at 150 and 600 °C. The resting influence on the mechanical properties of these samples was investigated. It was established that with increasing
of Tan and ε at Tdef |
|---|