The Tribological Characteristics of Ni-Cr Cast Alloy at 1000 Degree C in Air

Ni-Cr alloy sliding tests in the atmosphere at 1000 °C which is higher than the temperatures used in the conventional research were carried out and observed the process in which glazed oxide layer is formed on the wear track. By the analysis of the element distribution on the cross-section o...

Descripción completa

Guardado en:

Detalles Bibliográficos
Autores principales:	Junichi Yoshihisa, Fumihiko Yokoyama, Takahiro Yamasaki, Nobuo Ohmae
Formato:	article
Lenguaje:	EN
Publicado:	Japanese Society of Tribologists 2010
Materias:	ni-cr cast alloy glazed oxide high temperature oxidative wear Physics QC1-999 Engineering (General). Civil engineering (General) TA1-2040 Mechanical engineering and machinery TJ1-1570 Chemistry QD1-999
Acceso en línea:	https://doaj.org/article/5486c22dcb5d4103b0ec489198e2c87b
Etiquetas:	Agregar Etiqueta Sin Etiquetas, Sea el primero en etiquetar este registro!

id	oai:doaj.org-article:5486c22dcb5d4103b0ec489198e2c87b
record_format	dspace
spelling	oai:doaj.org-article:5486c22dcb5d4103b0ec489198e2c87b2021-11-05T09:27:17ZThe Tribological Characteristics of Ni-Cr Cast Alloy at 1000 Degree C in Air1881-219810.2474/trol.5.27https://doaj.org/article/5486c22dcb5d4103b0ec489198e2c87b2010-01-01T00:00:00Zhttps://www.jstage.jst.go.jp/article/trol/5/1/5_1_27/_pdf/-char/enhttps://doaj.org/toc/1881-2198Ni-Cr alloy sliding tests in the atmosphere at 1000 °C which is higher than the temperatures used in the conventional research were carried out and observed the process in which glazed oxide layer is formed on the wear track. By the analysis of the element distribution on the cross-section of the glazed oxide layer formed on the wear track after the friction had been reduced, we have clarified that the glazed oxide layer formation process is the same as the process found by the conventional research. Furthermore, the discharge of wear particle necessary for the formation of glazed oxide is further promoted at 1000 °C and therefore glazed oxide begins to form on the comparatively early stage, thereby showing low friction and low wear.Junichi YoshihisaFumihiko YokoyamaTakahiro YamasakiNobuo OhmaeJapanese Society of Tribologistsarticleni-cr cast alloyglazed oxidehigh temperatureoxidative wearPhysicsQC1-999Engineering (General). Civil engineering (General)TA1-2040Mechanical engineering and machineryTJ1-1570ChemistryQD1-999ENTribology Online, Vol 5, Iss 1, Pp 27-32 (2010)
institution	DOAJ
collection	DOAJ
language	EN
topic	ni-cr cast alloy glazed oxide high temperature oxidative wear Physics QC1-999 Engineering (General). Civil engineering (General) TA1-2040 Mechanical engineering and machinery TJ1-1570 Chemistry QD1-999
spellingShingle	ni-cr cast alloy glazed oxide high temperature oxidative wear Physics QC1-999 Engineering (General). Civil engineering (General) TA1-2040 Mechanical engineering and machinery TJ1-1570 Chemistry QD1-999 Junichi Yoshihisa Fumihiko Yokoyama Takahiro Yamasaki Nobuo Ohmae The Tribological Characteristics of Ni-Cr Cast Alloy at 1000 Degree C in Air
description	Ni-Cr alloy sliding tests in the atmosphere at 1000 °C which is higher than the temperatures used in the conventional research were carried out and observed the process in which glazed oxide layer is formed on the wear track. By the analysis of the element distribution on the cross-section of the glazed oxide layer formed on the wear track after the friction had been reduced, we have clarified that the glazed oxide layer formation process is the same as the process found by the conventional research. Furthermore, the discharge of wear particle necessary for the formation of glazed oxide is further promoted at 1000 °C and therefore glazed oxide begins to form on the comparatively early stage, thereby showing low friction and low wear.
format	article
author	Junichi Yoshihisa Fumihiko Yokoyama Takahiro Yamasaki Nobuo Ohmae
author_facet	Junichi Yoshihisa Fumihiko Yokoyama Takahiro Yamasaki Nobuo Ohmae
author_sort	Junichi Yoshihisa
title	The Tribological Characteristics of Ni-Cr Cast Alloy at 1000 Degree C in Air
title_short	The Tribological Characteristics of Ni-Cr Cast Alloy at 1000 Degree C in Air
title_full	The Tribological Characteristics of Ni-Cr Cast Alloy at 1000 Degree C in Air
title_fullStr	The Tribological Characteristics of Ni-Cr Cast Alloy at 1000 Degree C in Air
title_full_unstemmed	The Tribological Characteristics of Ni-Cr Cast Alloy at 1000 Degree C in Air
title_sort	tribological characteristics of ni-cr cast alloy at 1000 degree c in air
publisher	Japanese Society of Tribologists
publishDate	2010
url	https://doaj.org/article/5486c22dcb5d4103b0ec489198e2c87b
work_keys_str_mv	AT junichiyoshihisa thetribologicalcharacteristicsofnicrcastalloyat1000degreecinair AT fumihikoyokoyama thetribologicalcharacteristicsofnicrcastalloyat1000degreecinair AT takahiroyamasaki thetribologicalcharacteristicsofnicrcastalloyat1000degreecinair AT nobuoohmae thetribologicalcharacteristicsofnicrcastalloyat1000degreecinair AT junichiyoshihisa tribologicalcharacteristicsofnicrcastalloyat1000degreecinair AT fumihikoyokoyama tribologicalcharacteristicsofnicrcastalloyat1000degreecinair AT takahiroyamasaki tribologicalcharacteristicsofnicrcastalloyat1000degreecinair AT nobuoohmae tribologicalcharacteristicsofnicrcastalloyat1000degreecinair
_version_	1718444349268688896

The Tribological Characteristics of Ni-Cr Cast Alloy at 1000 Degree C in Air

Ejemplares similares