Effect of the Small Punch Test sample geometry on the Liquid Metal Embrittlement of Cu-30 wt% Zn by the eGaIn

Liquid metal embrittlement (LME) is the embrittlement or the modification of the fracture behaviour of a metal or alloy when it undergoes plastic deformation while in contact with a liquid metal or liquid alloy. LME occurrence depends strongly on the properties of the metals involved and on the cond...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Ezequiel Marco, Proriol Serre Ingrid
Formato: article
Lenguaje:EN
FR
Publicado: EDP Sciences 2021
Materias:
Acceso en línea:https://doaj.org/article/56de9116b5cd4a52a51d502bbdbc529d
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
id oai:doaj.org-article:56de9116b5cd4a52a51d502bbdbc529d
record_format dspace
spelling oai:doaj.org-article:56de9116b5cd4a52a51d502bbdbc529d2021-12-02T17:13:46ZEffect of the Small Punch Test sample geometry on the Liquid Metal Embrittlement of Cu-30 wt% Zn by the eGaIn2261-236X10.1051/matecconf/202134902014https://doaj.org/article/56de9116b5cd4a52a51d502bbdbc529d2021-01-01T00:00:00Zhttps://www.matec-conferences.org/articles/matecconf/pdf/2021/18/matecconf_iceaf2021_02014.pdfhttps://doaj.org/toc/2261-236XLiquid metal embrittlement (LME) is the embrittlement or the modification of the fracture behaviour of a metal or alloy when it undergoes plastic deformation while in contact with a liquid metal or liquid alloy. LME occurrence depends strongly on the properties of the metals involved and on the conditions of the mechanical stresses applied to the solid. The Small Punch Test (SPT) on flat specimens is very sensitive to identify the conditions of LME occurrence. Moreover, there are alternative SPT notched specimen geometries that have the potential to screen solid/liquid couples for sensibility to LME in different conditions. To study the apparition of the LME on an alpha brass with 30 wt% Zn in contact with the eGaIn (Ga-In eutectic), SPT at room temperature were carried out at different displacement rates and using three specimen types: the standard flat geometry and two notched geometries. While the flat specimens did not present LME, the presence of a notch and a high strain rate induced LME on the other specimen geometries. For these last specimens, the eGaIn modifies the SPT load-displacement curves at the crack propagation stage and changes the fracture to a partially ductile fracture followed by a brittle fracture.Ezequiel MarcoProriol Serre IngridEDP SciencesarticleEngineering (General). Civil engineering (General)TA1-2040ENFRMATEC Web of Conferences, Vol 349, p 02014 (2021)
institution DOAJ
collection DOAJ
language EN
FR
topic Engineering (General). Civil engineering (General)
TA1-2040
spellingShingle Engineering (General). Civil engineering (General)
TA1-2040
Ezequiel Marco
Proriol Serre Ingrid
Effect of the Small Punch Test sample geometry on the Liquid Metal Embrittlement of Cu-30 wt% Zn by the eGaIn
description Liquid metal embrittlement (LME) is the embrittlement or the modification of the fracture behaviour of a metal or alloy when it undergoes plastic deformation while in contact with a liquid metal or liquid alloy. LME occurrence depends strongly on the properties of the metals involved and on the conditions of the mechanical stresses applied to the solid. The Small Punch Test (SPT) on flat specimens is very sensitive to identify the conditions of LME occurrence. Moreover, there are alternative SPT notched specimen geometries that have the potential to screen solid/liquid couples for sensibility to LME in different conditions. To study the apparition of the LME on an alpha brass with 30 wt% Zn in contact with the eGaIn (Ga-In eutectic), SPT at room temperature were carried out at different displacement rates and using three specimen types: the standard flat geometry and two notched geometries. While the flat specimens did not present LME, the presence of a notch and a high strain rate induced LME on the other specimen geometries. For these last specimens, the eGaIn modifies the SPT load-displacement curves at the crack propagation stage and changes the fracture to a partially ductile fracture followed by a brittle fracture.
format article
author Ezequiel Marco
Proriol Serre Ingrid
author_facet Ezequiel Marco
Proriol Serre Ingrid
author_sort Ezequiel Marco
title Effect of the Small Punch Test sample geometry on the Liquid Metal Embrittlement of Cu-30 wt% Zn by the eGaIn
title_short Effect of the Small Punch Test sample geometry on the Liquid Metal Embrittlement of Cu-30 wt% Zn by the eGaIn
title_full Effect of the Small Punch Test sample geometry on the Liquid Metal Embrittlement of Cu-30 wt% Zn by the eGaIn
title_fullStr Effect of the Small Punch Test sample geometry on the Liquid Metal Embrittlement of Cu-30 wt% Zn by the eGaIn
title_full_unstemmed Effect of the Small Punch Test sample geometry on the Liquid Metal Embrittlement of Cu-30 wt% Zn by the eGaIn
title_sort effect of the small punch test sample geometry on the liquid metal embrittlement of cu-30 wt% zn by the egain
publisher EDP Sciences
publishDate 2021
url https://doaj.org/article/56de9116b5cd4a52a51d502bbdbc529d
work_keys_str_mv AT ezequielmarco effectofthesmallpunchtestsamplegeometryontheliquidmetalembrittlementofcu30wtznbytheegain
AT proriolserreingrid effectofthesmallpunchtestsamplegeometryontheliquidmetalembrittlementofcu30wtznbytheegain
_version_ 1718381319259422720