Pulp and paper making features of Sequoia sempervirens wood
In this research pulp and paper making characteristics of Sequoia sempervirens from Chamestan noor research station were studied. The dry and critical specific gravity of sap wood 0.352 and 0.324, heart wood 0.43 and 0.40, fiber length 2.01 mm. diameter 39.84µm. lumen 33.15µm and cell thickness wall...
Guardado en:
| Autores principales: | , , |
|---|---|
| Formato: | article |
| Lenguaje: | FA |
| Publicado: |
Regional Information Center for Science and Technology (RICeST)
2010
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/5a99dcc769f0499b80bec42faeca6912 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | In this research pulp and paper making characteristics of Sequoia sempervirens from Chamestan noor research station were studied. The dry and critical specific gravity of sap wood 0.352 and 0.324, heart wood 0.43 and 0.40, fiber length 2.01 mm. diameter 39.84µm. lumen 33.15µm and cell thickness wall 2.89µm were measured as respectively. The amount of cellulose of 52.63%, lignin 35.32%, ext. 6.68% and ash 0.45% were obtained as well. Kraft process was used for pulping. The yield of these pulps in 12% effective alkali were measured as 56% and in 18% effective alkali 39.69% respectively. In 3 hours of cooking time, the tear strength of these pulps 19.74 mNm2/gr and In 2 hours of cooking time 15.22 mNm2/gr respectively were measured. |
|---|