Influence of Different Acid on the Interfacial Compatibility between Rusted Steel and Water-Based Coating

We aimed to improve the corrosion resistance of transmission network cabinet equipment in high temperature and humidity environment. In this paper, using acid modified acrylic acid as the main component, the composite conversion agent was obtained by adding phosphoric acid phytic acid and other comp...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Wenbo Li, Yue Jiang, Dingguo Liu, Jiran Zhu, Yi Xie, Lanlan Liu
Formato: article
Lenguaje:EN
Publicado: MDPI AG 2021
Materias:
Acceso en línea:https://doaj.org/article/5b162428421347efaf25830ca2bc9811
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
Descripción
Sumario:We aimed to improve the corrosion resistance of transmission network cabinet equipment in high temperature and humidity environment. In this paper, using acid modified acrylic acid as the main component, the composite conversion agent was obtained by adding phosphoric acid phytic acid and other components. Through the surface morphology, electrochemical test and adhesion force test of rust conversion coating, the versatility and corrosion resistance of rust conversion coating on the substrates were analyzed. Combined with zinc phosphate primer, the effect of rust conversion agent on the adhesion and salt spray corrosion resistance of the commercial primers was studied. The composite conversion agent has good effect on atmospheric corrosion rust layer. The corrosion resistance and adhesion force of the atmospheric corrosion rust layer treated with rust conversion agent were significantly increased. The adhesion of zinc phosphate primer on atmospheric corrosion rust coating with rust conversion was three times higher than that of atmospheric corrosion rust coating without rust conversion, respectively. Composite rust conversion agent has broad versatility, which can be used for rust conversion of atmospheric corrosion rust layer. At the same time, it has a good corrosion resistance, that can obviously improve the corrosion potential of the corroded surface and reduce the corrosion current density. In addition, the composite rust conversion agent can significantly improve the adhesion and corrosion resistance of the primer coating.