Influence of Different Acid on the Interfacial Compatibility between Rusted Steel and Water-Based Coating
We aimed to improve the corrosion resistance of transmission network cabinet equipment in high temperature and humidity environment. In this paper, using acid modified acrylic acid as the main component, the composite conversion agent was obtained by adding phosphoric acid phytic acid and other comp...
Guardado en:
Autores principales: | , , , , , |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
MDPI AG
2021
|
Materias: | |
Acceso en línea: | https://doaj.org/article/5b162428421347efaf25830ca2bc9811 |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
id |
oai:doaj.org-article:5b162428421347efaf25830ca2bc9811 |
---|---|
record_format |
dspace |
spelling |
oai:doaj.org-article:5b162428421347efaf25830ca2bc98112021-11-25T17:16:57ZInfluence of Different Acid on the Interfacial Compatibility between Rusted Steel and Water-Based Coating10.3390/coatings111114122079-6412https://doaj.org/article/5b162428421347efaf25830ca2bc98112021-11-01T00:00:00Zhttps://www.mdpi.com/2079-6412/11/11/1412https://doaj.org/toc/2079-6412We aimed to improve the corrosion resistance of transmission network cabinet equipment in high temperature and humidity environment. In this paper, using acid modified acrylic acid as the main component, the composite conversion agent was obtained by adding phosphoric acid phytic acid and other components. Through the surface morphology, electrochemical test and adhesion force test of rust conversion coating, the versatility and corrosion resistance of rust conversion coating on the substrates were analyzed. Combined with zinc phosphate primer, the effect of rust conversion agent on the adhesion and salt spray corrosion resistance of the commercial primers was studied. The composite conversion agent has good effect on atmospheric corrosion rust layer. The corrosion resistance and adhesion force of the atmospheric corrosion rust layer treated with rust conversion agent were significantly increased. The adhesion of zinc phosphate primer on atmospheric corrosion rust coating with rust conversion was three times higher than that of atmospheric corrosion rust coating without rust conversion, respectively. Composite rust conversion agent has broad versatility, which can be used for rust conversion of atmospheric corrosion rust layer. At the same time, it has a good corrosion resistance, that can obviously improve the corrosion potential of the corroded surface and reduce the corrosion current density. In addition, the composite rust conversion agent can significantly improve the adhesion and corrosion resistance of the primer coating.Wenbo LiYue JiangDingguo LiuJiran ZhuYi XieLanlan LiuMDPI AGarticlerust conversioncorrosion resistanceadhesionEngineering (General). Civil engineering (General)TA1-2040ENCoatings, Vol 11, Iss 1412, p 1412 (2021) |
institution |
DOAJ |
collection |
DOAJ |
language |
EN |
topic |
rust conversion corrosion resistance adhesion Engineering (General). Civil engineering (General) TA1-2040 |
spellingShingle |
rust conversion corrosion resistance adhesion Engineering (General). Civil engineering (General) TA1-2040 Wenbo Li Yue Jiang Dingguo Liu Jiran Zhu Yi Xie Lanlan Liu Influence of Different Acid on the Interfacial Compatibility between Rusted Steel and Water-Based Coating |
description |
We aimed to improve the corrosion resistance of transmission network cabinet equipment in high temperature and humidity environment. In this paper, using acid modified acrylic acid as the main component, the composite conversion agent was obtained by adding phosphoric acid phytic acid and other components. Through the surface morphology, electrochemical test and adhesion force test of rust conversion coating, the versatility and corrosion resistance of rust conversion coating on the substrates were analyzed. Combined with zinc phosphate primer, the effect of rust conversion agent on the adhesion and salt spray corrosion resistance of the commercial primers was studied. The composite conversion agent has good effect on atmospheric corrosion rust layer. The corrosion resistance and adhesion force of the atmospheric corrosion rust layer treated with rust conversion agent were significantly increased. The adhesion of zinc phosphate primer on atmospheric corrosion rust coating with rust conversion was three times higher than that of atmospheric corrosion rust coating without rust conversion, respectively. Composite rust conversion agent has broad versatility, which can be used for rust conversion of atmospheric corrosion rust layer. At the same time, it has a good corrosion resistance, that can obviously improve the corrosion potential of the corroded surface and reduce the corrosion current density. In addition, the composite rust conversion agent can significantly improve the adhesion and corrosion resistance of the primer coating. |
format |
article |
author |
Wenbo Li Yue Jiang Dingguo Liu Jiran Zhu Yi Xie Lanlan Liu |
author_facet |
Wenbo Li Yue Jiang Dingguo Liu Jiran Zhu Yi Xie Lanlan Liu |
author_sort |
Wenbo Li |
title |
Influence of Different Acid on the Interfacial Compatibility between Rusted Steel and Water-Based Coating |
title_short |
Influence of Different Acid on the Interfacial Compatibility between Rusted Steel and Water-Based Coating |
title_full |
Influence of Different Acid on the Interfacial Compatibility between Rusted Steel and Water-Based Coating |
title_fullStr |
Influence of Different Acid on the Interfacial Compatibility between Rusted Steel and Water-Based Coating |
title_full_unstemmed |
Influence of Different Acid on the Interfacial Compatibility between Rusted Steel and Water-Based Coating |
title_sort |
influence of different acid on the interfacial compatibility between rusted steel and water-based coating |
publisher |
MDPI AG |
publishDate |
2021 |
url |
https://doaj.org/article/5b162428421347efaf25830ca2bc9811 |
work_keys_str_mv |
AT wenboli influenceofdifferentacidontheinterfacialcompatibilitybetweenrustedsteelandwaterbasedcoating AT yuejiang influenceofdifferentacidontheinterfacialcompatibilitybetweenrustedsteelandwaterbasedcoating AT dingguoliu influenceofdifferentacidontheinterfacialcompatibilitybetweenrustedsteelandwaterbasedcoating AT jiranzhu influenceofdifferentacidontheinterfacialcompatibilitybetweenrustedsteelandwaterbasedcoating AT yixie influenceofdifferentacidontheinterfacialcompatibilitybetweenrustedsteelandwaterbasedcoating AT lanlanliu influenceofdifferentacidontheinterfacialcompatibilitybetweenrustedsteelandwaterbasedcoating |
_version_ |
1718412531391791104 |