Investigation of 9000 hours multi-stress aging effects on High-Temperature Vulcanized Silicone Rubber with silica (nano/micro) filler hybrid composite insulator.

Degradation in the polymeric insulators is caused due to the environmental stresses. The main aim of this paper is to explore the improved aging characteristics of hybrid samples by adding nano/micro silica in High Temperature Vulcanized Silicone Rubber (HTV-SiR) under long term accelerated aging co...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Arooj Rashid, Jawad Saleem, Muhammad Amin, Sahibzada Muhammad Ali, Aftab Ahmad Khan, Muhammad Bilal Qureshi, Sara Ali, Darren Dancey, Raheel Nawaz
Formato: article
Lenguaje:EN
Publicado: Public Library of Science (PLoS) 2021
Materias:
R
Q
Acceso en línea:https://doaj.org/article/5d918da8f0d441058f2fd8c335294727
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
id oai:doaj.org-article:5d918da8f0d441058f2fd8c335294727
record_format dspace
spelling oai:doaj.org-article:5d918da8f0d441058f2fd8c3352947272021-12-02T20:04:48ZInvestigation of 9000 hours multi-stress aging effects on High-Temperature Vulcanized Silicone Rubber with silica (nano/micro) filler hybrid composite insulator.1932-620310.1371/journal.pone.0253372https://doaj.org/article/5d918da8f0d441058f2fd8c3352947272021-01-01T00:00:00Zhttps://doi.org/10.1371/journal.pone.0253372https://doaj.org/toc/1932-6203Degradation in the polymeric insulators is caused due to the environmental stresses. The main aim of this paper is to explore the improved aging characteristics of hybrid samples by adding nano/micro silica in High Temperature Vulcanized Silicone Rubber (HTV-SiR) under long term accelerated aging conditions for 9000 hours. As HTV-SiR is unable to sustain environmental stresses for a long time, thus a long term accelerated aging behavior is an important phenomenon to be considered for field application. The aging characteristics of nano/micro filled HTV-SiR are analyzed by using techniques such as Scanning Electron Microscopy (SEM), Leakage Current (LC), Fourier Transform Infrared Microscopy (FTIR), Hydrophobicity Classification (HC), and breakdown strength for the aging time of 9000 hours. FTIR and leakage currents are measured after every cycle. All the co-filled samples revealed escalated aging characteristics as compared to the neat sample except the SN8 sample (8% nano-silica+20% micro-silica) after 9000 hours of aging. The highest loading of 6% and 8% nano-silica with 20% micro-silica do not contribute to the improved performance when compared with the neat and hybrid samples. However, from the critical experimental analysis, it is deduced that SN2 sample (2% nano-silica+20% micro-silica) is highly resistant to the long term accelerated aging conditions. SN2 has no cracks, lower loss percentages in the important FTIR absorption peaks, higher breakdown strength and superior HC after aging as compared to the unfilled and hybrid samples.Arooj RashidJawad SaleemMuhammad AminSahibzada Muhammad AliAftab Ahmad KhanMuhammad Bilal QureshiSara AliDarren DanceyRaheel NawazPublic Library of Science (PLoS)articleMedicineRScienceQENPLoS ONE, Vol 16, Iss 7, p e0253372 (2021)
institution DOAJ
collection DOAJ
language EN
topic Medicine
R
Science
Q
spellingShingle Medicine
R
Science
Q
Arooj Rashid
Jawad Saleem
Muhammad Amin
Sahibzada Muhammad Ali
Aftab Ahmad Khan
Muhammad Bilal Qureshi
Sara Ali
Darren Dancey
Raheel Nawaz
Investigation of 9000 hours multi-stress aging effects on High-Temperature Vulcanized Silicone Rubber with silica (nano/micro) filler hybrid composite insulator.
description Degradation in the polymeric insulators is caused due to the environmental stresses. The main aim of this paper is to explore the improved aging characteristics of hybrid samples by adding nano/micro silica in High Temperature Vulcanized Silicone Rubber (HTV-SiR) under long term accelerated aging conditions for 9000 hours. As HTV-SiR is unable to sustain environmental stresses for a long time, thus a long term accelerated aging behavior is an important phenomenon to be considered for field application. The aging characteristics of nano/micro filled HTV-SiR are analyzed by using techniques such as Scanning Electron Microscopy (SEM), Leakage Current (LC), Fourier Transform Infrared Microscopy (FTIR), Hydrophobicity Classification (HC), and breakdown strength for the aging time of 9000 hours. FTIR and leakage currents are measured after every cycle. All the co-filled samples revealed escalated aging characteristics as compared to the neat sample except the SN8 sample (8% nano-silica+20% micro-silica) after 9000 hours of aging. The highest loading of 6% and 8% nano-silica with 20% micro-silica do not contribute to the improved performance when compared with the neat and hybrid samples. However, from the critical experimental analysis, it is deduced that SN2 sample (2% nano-silica+20% micro-silica) is highly resistant to the long term accelerated aging conditions. SN2 has no cracks, lower loss percentages in the important FTIR absorption peaks, higher breakdown strength and superior HC after aging as compared to the unfilled and hybrid samples.
format article
author Arooj Rashid
Jawad Saleem
Muhammad Amin
Sahibzada Muhammad Ali
Aftab Ahmad Khan
Muhammad Bilal Qureshi
Sara Ali
Darren Dancey
Raheel Nawaz
author_facet Arooj Rashid
Jawad Saleem
Muhammad Amin
Sahibzada Muhammad Ali
Aftab Ahmad Khan
Muhammad Bilal Qureshi
Sara Ali
Darren Dancey
Raheel Nawaz
author_sort Arooj Rashid
title Investigation of 9000 hours multi-stress aging effects on High-Temperature Vulcanized Silicone Rubber with silica (nano/micro) filler hybrid composite insulator.
title_short Investigation of 9000 hours multi-stress aging effects on High-Temperature Vulcanized Silicone Rubber with silica (nano/micro) filler hybrid composite insulator.
title_full Investigation of 9000 hours multi-stress aging effects on High-Temperature Vulcanized Silicone Rubber with silica (nano/micro) filler hybrid composite insulator.
title_fullStr Investigation of 9000 hours multi-stress aging effects on High-Temperature Vulcanized Silicone Rubber with silica (nano/micro) filler hybrid composite insulator.
title_full_unstemmed Investigation of 9000 hours multi-stress aging effects on High-Temperature Vulcanized Silicone Rubber with silica (nano/micro) filler hybrid composite insulator.
title_sort investigation of 9000 hours multi-stress aging effects on high-temperature vulcanized silicone rubber with silica (nano/micro) filler hybrid composite insulator.
publisher Public Library of Science (PLoS)
publishDate 2021
url https://doaj.org/article/5d918da8f0d441058f2fd8c335294727
work_keys_str_mv AT aroojrashid investigationof9000hoursmultistressagingeffectsonhightemperaturevulcanizedsiliconerubberwithsilicananomicrofillerhybridcompositeinsulator
AT jawadsaleem investigationof9000hoursmultistressagingeffectsonhightemperaturevulcanizedsiliconerubberwithsilicananomicrofillerhybridcompositeinsulator
AT muhammadamin investigationof9000hoursmultistressagingeffectsonhightemperaturevulcanizedsiliconerubberwithsilicananomicrofillerhybridcompositeinsulator
AT sahibzadamuhammadali investigationof9000hoursmultistressagingeffectsonhightemperaturevulcanizedsiliconerubberwithsilicananomicrofillerhybridcompositeinsulator
AT aftabahmadkhan investigationof9000hoursmultistressagingeffectsonhightemperaturevulcanizedsiliconerubberwithsilicananomicrofillerhybridcompositeinsulator
AT muhammadbilalqureshi investigationof9000hoursmultistressagingeffectsonhightemperaturevulcanizedsiliconerubberwithsilicananomicrofillerhybridcompositeinsulator
AT saraali investigationof9000hoursmultistressagingeffectsonhightemperaturevulcanizedsiliconerubberwithsilicananomicrofillerhybridcompositeinsulator
AT darrendancey investigationof9000hoursmultistressagingeffectsonhightemperaturevulcanizedsiliconerubberwithsilicananomicrofillerhybridcompositeinsulator
AT raheelnawaz investigationof9000hoursmultistressagingeffectsonhightemperaturevulcanizedsiliconerubberwithsilicananomicrofillerhybridcompositeinsulator
_version_ 1718375544646533120