Effect Ti/AlTiN Multilayer Coating on the Crater Wear Process of Cutting Tool and Tribological Properties

Tool wear is a major problem in machining operations because the resulting material loss gradually changes of the machine tool. There many factors may leads to material loss like; friction, corrosion, and also it’s happened by rubbing during machining processes between the work piece and the tool....

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Kamil J. Kadhim, Abbas Allawi Abbas, Maher Ali H Hussein
Formato: article
Lenguaje:EN
Publicado: Al-Khwarizmi College of Engineering – University of Baghdad 2018
Materias:
Acceso en línea:https://doaj.org/article/6230d8544340424e9590ef92c34a75e3
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
Descripción
Sumario:Tool wear is a major problem in machining operations because the resulting material loss gradually changes of the machine tool. There many factors may leads to material loss like; friction, corrosion, and also it’s happened by rubbing during machining processes between the work piece and the tool. Dimensional accuracy of the work piece, and also the surface finish will be reducing by tool wear. It can also increase cutting force. In this study, we focused on the effect of the coating process on crater wear problems. Crater wear is caused by the flow between the chip and the rake face of the tool, whereas flank wear is caused by the contact between the tool and the work piece. In reducing crater wear, aluminum titanium nitride (AlTiN) using Al0.67 Ti0.33 in cathodic arc plating system is considered effective as a tools coating material. In reducing flank wear, AlTiN is also deemed as the best tool coating material. Experimentally, the use of Ti/AlTiN-coated tools has been proven effective in reducing crater wear. In this study, the roughness Ra values of the (Ti/AlTiN) coatings were (0.14, 0.15, 0.23, 0.02, 0.21) µm at values of layers thickness (1.138, 1.518, 1.735, 2.717, 3.0818) µm, respectively. The lowest COF appeared at thickness 2.717 µm and the high coefficient of friction of the Ti/AlTiN coating was a result of high roughness and the large contact surface area of the system coating steel ball. The two most important parameters used to measure crater wear are length and width of wear.