Closed-Cell Powder Metallurgical Aluminium Foams Reinforced with 3 vol.% SiC and 3 vol.% Graphite
Closed-cell aluminium foams (nominal composition: AlSi12Mg0.6Fe0.3) were prepared by the powder metallurgical route (using 0.4 wt.% TiH<sub>2</sub> untreated powder as the foaming agent). Pure foams and foams with the addition of 3 vol.% graphite or SiC powder were prepared. The microstr...
Guardado en:
| Autores principales: | , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
MDPI AG
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/65c74670a7564192803943ab1d51b375 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Closed-cell aluminium foams (nominal composition: AlSi12Mg0.6Fe0.3) were prepared by the powder metallurgical route (using 0.4 wt.% TiH<sub>2</sub> untreated powder as the foaming agent). Pure foams and foams with the addition of 3 vol.% graphite or SiC powder were prepared. The microstructure and mechanical properties of the prepared aluminium foams containing reinforcing particles were investigated at constant density and compared to those of the pure foam. Vibration measurements were performed to determine the damping properties and modulus of elasticity of the foams. Uniaxial compression tests were performed to determine the following mechanical properties: collapse stress, efficiency of energy absorption, plateau length and densification strain of the foams. All the foams behaved in a brittle manner during compression. Finally, the effect of admixed graphite and SiC powders on the properties of the investigated foam was evaluated, discussed and modelled. The addition of powders changed all investigated properties of the foams. Only the efficiency of energy absorption at constant density was almost identical. |
|---|