Corrosion Behavior of Chromium Coated Zy-4 Cladding under CANDU Primary Circuit Conditions
The manuscript is focused on corrosion behavior of a Cr coating under CANada Deuterium Uranium(CANDU) primary circuit conditions. The Cr coating is obtained via the thermionic vacuum arc procedure on Zircaloy -4 cladding. The surface coating characterization was performed using metallographic analys...
Guardado en:
| Autores principales: | , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
MDPI AG
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/681cd22dae8a4133865959eb57d8c885 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | The manuscript is focused on corrosion behavior of a Cr coating under CANada Deuterium Uranium(CANDU) primary circuit conditions. The Cr coating is obtained via the thermionic vacuum arc procedure on Zircaloy -4 cladding. The surface coating characterization was performed using metallographic analysis and scanning electron microscopy (SEM) with an energy dispersive spectra detector (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) investigations. The thickness of the Cr coating determined from SEM images is around 500 nm layers After the autoclaving period, the thickness of the samples increased in time slowly. The kinetic of oxidation established a logarithmic oxidation law. The corrosion tests for various autoclaving periods of time include electrochemical impedance spectroscopy (EIS) and potentiodynamic tests, permitting computing porosity and efficiency of protection. All surface investigations sustain electrochemical results and promote the Cr coating on Zircaloy-4 alloy autoclaved for 3024 h as the best corrosion resistance based on decrease in corrosion current density values simultaneously with the increase of the time spent in autoclave. A slow increase of Vickers micro hardness was observed as a function of the autoclaved period as well. The value reached for 3024 h being 219 Kgf/mm<sup>2</sup> compared with 210 Kgf/mm<sup>2</sup> value before autoclaving. |
|---|