Effect of Ferritic Morphology on Yield Strength of CGHAZ in a Low Carbon Mo-V-N-Ti-B Steel

For investigating the impact of ferritic morphology on yield strength (YS) of the high-heat-input welding induced coarse-grained heat-affected zone (CGHAZ) of a low carbon Mo-V-N-Ti-B steel, a group of particular welding heat inputs were designed to obtain different ferritic microstructures in CGHAZ...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Leping Wang, Huibing Fan, Genhao Shi, Qiuming Wang, Qingfeng Wang, Fucheng Zhang
Formato: article
Lenguaje:EN
Publicado: MDPI AG 2021
Materias:
Acceso en línea:https://doaj.org/article/685b3692fb004c1dba4bb209c31b18f0
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
Descripción
Sumario:For investigating the impact of ferritic morphology on yield strength (YS) of the high-heat-input welding induced coarse-grained heat-affected zone (CGHAZ) of a low carbon Mo-V-N-Ti-B steel, a group of particular welding heat inputs were designed to obtain different ferritic microstructures in CGHAZ. The tensile properties were estimated from typical samples with ferritic microstructures. The mixed microstructures dominated by the intragranular polygonal ferrite (IGPF), the intragranular acicular ferrite (IGAF), and the granular bainite (GB) were obtained at the heat inputs of 35, 65, 85 and 120 kJ/cm, respectively. When the main microstructure changed from IGPF to IGAF and GB, YS increased first and then decreased. The microstructure consisting mainly of IGAF possessed the maximum YS. As the main microstructure changed from IGPF to IGAF and GB, the contribution of grain refinement strengthening to YS was estimated to be elevated remarkably. This means the strength of CGHAZ in a low-carbon steel subjected to the high-heat-input welding could be enhanced by promoting the fine-grained AF and GB formation.