Artificial polyhydroxyalkanoate poly[2-hydroxybutyrate-block-3-hydroxybutyrate] elastomer-like material
Abstract The first polyhydroxyalkanoate (PHA) block copolymer poly(2-hydroxybutyrate-b-3-hydroxybutyrate) [P(2HB-b-3HB)] was previously synthesized using engineered Escherichia coli expressing a chimeric PHA synthase PhaCAR with monomer sequence-regulating capacity. In the present study, the physica...
Guardado en:
| Autores principales: | , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Nature Portfolio
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/6ba9606d1b4642c8824c9b9896d10447 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Abstract The first polyhydroxyalkanoate (PHA) block copolymer poly(2-hydroxybutyrate-b-3-hydroxybutyrate) [P(2HB-b-3HB)] was previously synthesized using engineered Escherichia coli expressing a chimeric PHA synthase PhaCAR with monomer sequence-regulating capacity. In the present study, the physical properties of the block copolymer and its relevant random copolymer P(2HB-ran-3HB) were evaluated. Stress–strain tests on the P(88 mol% 2HB-b-3HB) film showed an increasing stress value during elongation up to 393%. In addition, the block copolymer film exhibited slow contraction behavior after elongation, indicating that P(2HB-b-3HB) is an elastomer-like material. In contrast, the P(92 mol% 2HB-ran-3HB) film, which was stretched up to 692% with nearly constant stress, was stretchable but not elastic. The differential scanning calorimetry and wide-angle X-ray diffraction analyses indicated that the P(2HB-b-3HB) contained the amorphous P(2HB) phase and the crystalline P(3HB) phase, whereas P(2HB-ran-3HB) was wholly amorphous. Therefore, the elasticity of P(2HB-b-3HB) can be attributed to the presence of the crystalline P(3HB) phase and a noncovalent crosslinked structure by the crystals. These results show the potential of block PHAs as elastic materials. |
|---|