Complex-mediated microwave-assisted synthesis of polyacrylonitrile nanoparticles
Trinath Biswal, Ramakanta Samal, Prafulla K SahooDepartment of Chemistry, Utkal University, Vani Vihar, Bhubaneswar 751004, IndiaAbstract: The polymerization of acrylonitrile (AN) is efficiently, easily, and quickly achieved in the presence of trans-[Co(III)en2Cl2]Cl complex in a domestic microwave...
Guardado en:
| Autores principales: | , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Dove Medical Press
2010
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/7236c0c048f24d7ba86cbaf337d2ab91 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Trinath Biswal, Ramakanta Samal, Prafulla K SahooDepartment of Chemistry, Utkal University, Vani Vihar, Bhubaneswar 751004, IndiaAbstract: The polymerization of acrylonitrile (AN) is efficiently, easily, and quickly achieved in the presence of trans-[Co(III)en2Cl2]Cl complex in a domestic microwave (MW) oven. MW irradiation notably promoted the polymerization reaction; this phenomenon is ascribed to the acceleration of the initiator, ammonium persulfate (APS), decomposition by microwave irradiation in the presence of [Co(III)en2Cl2]Cl. The conversion of monomer to the polymer was mostly excellent in gram scale. Irradiation at low power and time produced more homogeneous polymers with high molecular weight and low polydispersity when compared with the polymer formed by a conventional heating method. The interaction of reacting components was monitored by UV-visible spectrometer. The average molecular weight was derived by gel permeation chromatography (GPC), viscosity methods, and sound velocity by ultrasonic interferometer. The uniform and reduced molecular size was characterized by transmission electron microscopy, the diameter of polyacrylonitrile nanoparticles (PAN) being in the range 50–115 nm and 40–230 nm in microwave and conventional heating methods respectively. The surface morphology of PAN prepared by MW irradiation was characterized by scanning electron microscope (SEM). From the kinetic results, the rate of polymerization (Rp) was expressed as Rp = [AN]0.63 [APS]0.57 [complex (I)].0.88Keywords: microwave, complex catalyst, nanoparticle, kinetics |
|---|