Experimental Investigation into the Strength of Single Sided Silicone Glazing Joints Under Blast Loading
An experimental study has taken place to quantify the strength of single sided structural silicone glazing joints under blast loading. The structural silicone specimens in this experiment were tested using a high-speed servo-hydraulic test machine at varying rates, representative of that experience...
Guardado en:
Autores principales: | , , , , , , , |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
Challenging Glass Conference
2016
|
Materias: | |
Acceso en línea: | https://doaj.org/article/7f8deb07264e4ab48ae0aa45ecb2b053 |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
id |
oai:doaj.org-article:7f8deb07264e4ab48ae0aa45ecb2b053 |
---|---|
record_format |
dspace |
spelling |
oai:doaj.org-article:7f8deb07264e4ab48ae0aa45ecb2b0532021-12-04T05:12:40ZExperimental Investigation into the Strength of Single Sided Silicone Glazing Joints Under Blast Loading10.7480/cgc.5.22562589-8019https://doaj.org/article/7f8deb07264e4ab48ae0aa45ecb2b0532016-06-01T00:00:00Zhttps://proceedings.challengingglass.com/index.php/cgc/article/view/147https://doaj.org/toc/2589-8019 An experimental study has taken place to quantify the strength of single sided structural silicone glazing joints under blast loading. The structural silicone specimens in this experiment were tested using a high-speed servo-hydraulic test machine at varying rates, representative of that experienced in a blast. Tests were conducted at displacement rates of 1m/s, 2m/s and 4m/s. The load was applied at two different angles of 30° and 45°. The tests were carried out on samples with different bite depths. The load was measured and the strength of the silicone joint was calculated at different testing rates. For a given testing rate and loading angle, the strength was found to be constant for different bite depths. The strength also showed an escalation at higher displacement rates. For the loading angles tested, there was no correlation found between the angle of loading and the strength. Through the measurement of displacement during the test, the work done on the silicone joint was also calculated. M.A. SamieianD. CormieF. DoebbelD. SmithW. WholeyB.R.K. BlackmanP.A. HooperJ.P. DearChallenging Glass ConferencearticleLaminatedGlassSiliconeJointsBlastClay industries. Ceramics. GlassTP785-869ENChallenging Glass Conference Proceedings, Vol 5 (2016) |
institution |
DOAJ |
collection |
DOAJ |
language |
EN |
topic |
Laminated Glass Silicone Joints Blast Clay industries. Ceramics. Glass TP785-869 |
spellingShingle |
Laminated Glass Silicone Joints Blast Clay industries. Ceramics. Glass TP785-869 M.A. Samieian D. Cormie F. Doebbel D. Smith W. Wholey B.R.K. Blackman P.A. Hooper J.P. Dear Experimental Investigation into the Strength of Single Sided Silicone Glazing Joints Under Blast Loading |
description |
An experimental study has taken place to quantify the strength of single sided structural silicone glazing joints under blast loading. The structural silicone specimens in this experiment were tested using a high-speed servo-hydraulic test machine at varying rates, representative of that experienced in a blast. Tests were conducted at displacement rates of 1m/s, 2m/s and 4m/s. The load was applied at two different angles of 30° and 45°. The tests were carried out on samples with different bite depths. The load was measured and the strength of the silicone joint was calculated at different testing rates. For a given testing rate and loading angle, the strength was found to be constant for different bite depths. The strength also showed an escalation at higher displacement rates. For the loading angles tested, there was no correlation found between the angle of loading and the strength. Through the measurement of displacement during the test, the work done on the silicone joint was also calculated.
|
format |
article |
author |
M.A. Samieian D. Cormie F. Doebbel D. Smith W. Wholey B.R.K. Blackman P.A. Hooper J.P. Dear |
author_facet |
M.A. Samieian D. Cormie F. Doebbel D. Smith W. Wholey B.R.K. Blackman P.A. Hooper J.P. Dear |
author_sort |
M.A. Samieian |
title |
Experimental Investigation into the Strength of Single Sided Silicone Glazing Joints Under Blast Loading |
title_short |
Experimental Investigation into the Strength of Single Sided Silicone Glazing Joints Under Blast Loading |
title_full |
Experimental Investigation into the Strength of Single Sided Silicone Glazing Joints Under Blast Loading |
title_fullStr |
Experimental Investigation into the Strength of Single Sided Silicone Glazing Joints Under Blast Loading |
title_full_unstemmed |
Experimental Investigation into the Strength of Single Sided Silicone Glazing Joints Under Blast Loading |
title_sort |
experimental investigation into the strength of single sided silicone glazing joints under blast loading |
publisher |
Challenging Glass Conference |
publishDate |
2016 |
url |
https://doaj.org/article/7f8deb07264e4ab48ae0aa45ecb2b053 |
work_keys_str_mv |
AT masamieian experimentalinvestigationintothestrengthofsinglesidedsiliconeglazingjointsunderblastloading AT dcormie experimentalinvestigationintothestrengthofsinglesidedsiliconeglazingjointsunderblastloading AT fdoebbel experimentalinvestigationintothestrengthofsinglesidedsiliconeglazingjointsunderblastloading AT dsmith experimentalinvestigationintothestrengthofsinglesidedsiliconeglazingjointsunderblastloading AT wwholey experimentalinvestigationintothestrengthofsinglesidedsiliconeglazingjointsunderblastloading AT brkblackman experimentalinvestigationintothestrengthofsinglesidedsiliconeglazingjointsunderblastloading AT pahooper experimentalinvestigationintothestrengthofsinglesidedsiliconeglazingjointsunderblastloading AT jpdear experimentalinvestigationintothestrengthofsinglesidedsiliconeglazingjointsunderblastloading |
_version_ |
1718372865334575104 |