Interaction of Corrosion-Cumulative Fatigue and Shot Peening of 1100-H12 Aluminum Alloy
Corrosion-fatigue occurs by the combined actions of cyclic loading and corrosive environment. The effect of shot peening on cumulative corrosion-fatigue life of 1100-H12 Al alloy was investigated. Before fatigue testing, specimens were submerged in 3.5%NaCl solution for 71 days. Constant fatigue tes...
Guardado en:
Autores principales: | Alalkawi H.J.M, Amer Hameed Maajeed, Zainab Azeez Betti |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
Al-Khwarizmi College of Engineering – University of Baghdad
2015
|
Materias: | |
Acceso en línea: | https://doaj.org/article/8a461a4bcbaa40a5a037f14fda577409 |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares
-
Interaction of Corrosion-Cumulative Fatigue and Shot Peening of 1100-H12 Aluminum Alloy
por: H .J.M Alalkawi, et al.
Publicado: (2015) -
A new Cumulative Damage Model for Fatigue Life Prediction under Shot Peening Treatment
por: Abdul-Jabar H. Ali, et al.
Publicado: (2015) -
Effect of optimal shot peening time on fatigue life for aluminum alloy 6061-T651
por: Ahmed N. Al-Khazraji
Publicado: (2019) -
A new Cumulative Damage Model for Fatigue Life Prediction under Shot Peening Treatment
por: Hussain J. M.Alalkawi, et al.
Publicado: (2017) -
Analysis of the Effects of Aggressive Shot Peening on Fatigue Life of 7075 T6 Aluminum Alloy
por: Khairallah S. Jabur
Publicado: (2012)