Effects of Sintering Temperature on Crystallization and Fabrication of Porous Bioactive Glass Scaffolds for Bone Regeneration
Abstract In this work the sintering ability of borosilicate (S53B50), borophosphate (P40B10) and phosphate (Sr) bioactive glasses was investigated. The glass powders were crushed and sintered in air at a heating rate of 10 °C/min for 2 hours at sintering temperatures between 480 °C–600 °C. The aim w...
Guardado en:
Autores principales: | E. P. Erasmus, O. T. Johnson, I. Sigalas, J. Massera |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
Nature Portfolio
2017
|
Materias: | |
Acceso en línea: | https://doaj.org/article/9865242f7dc043109f495e43d2cf590f |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares
-
Composite scaffolds of mesoporous bioactive glass and polyamide for bone repair
por: Su J, et al.
Publicado: (2012) -
Mesoporous bioactive glass surface modified poly(lactic-co-glycolic acid) electrospun fibrous scaffold for bone regeneration
por: Chen SJ, et al.
Publicado: (2015) -
In vivo experimental study on bone regeneration in critical bone defects using PIB nanogels/boron-containing mesoporous bioactive glass composite scaffold
por: Chen XH, et al.
Publicado: (2015) -
Periodontal regeneration using strontium-loaded mesoporous bioactive glass scaffolds in osteoporotic rats.
por: Yufeng Zhang, et al.
Publicado: (2014) -
Selective laser sintering fabrication of nano-hydroxyapatite/poly-ε-caprolactone scaffolds for bone tissue engineering applications
por: Xia Y, et al.
Publicado: (2013)