Micromechanisms of Deformation and Fracture in Porous L-PBF 316L Stainless Steel at Different Strain Rates

The process of an unstable plastic flow associated with the strain rate sensitivity of mechanical properties was studied in porous 316L austenitic steel samples manufactured by laser powder bed fusion (L-PBF). Different micromechanisms of deformation and fracture of porous samples dependent on strai...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Nataliya Kazantseva, Pavel Krakhmalev, Mikael Åsberg, Yulia Koemets, Maxim Karabanalov, Denis Davydov, Igor Ezhov, Olga Koemets
Formato: article
Lenguaje:EN
Publicado: MDPI AG 2021
Materias:
Acceso en línea:https://doaj.org/article/9afc122180a448fabe775a0a22878c99
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
Descripción
Sumario:The process of an unstable plastic flow associated with the strain rate sensitivity of mechanical properties was studied in porous 316L austenitic steel samples manufactured by laser powder bed fusion (L-PBF). Different micromechanisms of deformation and fracture of porous samples dependent on strain rate were found. It was found that despite the porosity, the specimens showed high strength, which increased with the loading rate. Porosity led to lower ductility of the studied specimens, in comparison with literature data for low porous 316L L-PBF samples and resulted in de-localization of plastic deformation. With an increase in strain rate, nucleation of new pores was less pronounced, so that at the highest strain rate of 8 × 10<sup>−3</sup> s<sup>−1</sup>, only pore coalescence was observed as the dominating microscopic mechanism of ductile fracture.