Influence of super-gravity coefficient on spatial distribution of solidification structure in Al-14.5Si alloys
We reported the influence of super-gravity field on spatial distribution of eutectic structure in Al-14.5Si alloys. The Al-14.5Si alloys were solidified under normal gravity (1 g) and various super-gravity fields (1000 g, 2000 g, 3000 g, 4000 g and 5000 g, g = 9.8 m/s2), respectively. The results in...
Guardado en:
| Autores principales: | , , , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Elsevier
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/9f3ed3e089474372bc5d087cced916bd |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | We reported the influence of super-gravity field on spatial distribution of eutectic structure in Al-14.5Si alloys. The Al-14.5Si alloys were solidified under normal gravity (1 g) and various super-gravity fields (1000 g, 2000 g, 3000 g, 4000 g and 5000 g, g = 9.8 m/s2), respectively. The results indicated that the homogeneous distribution of eutectic Si could be observed in the core region of the samples solidified under super-gravity field. As the coefficient of gravity increased, the eutectic Si was significantly refined, resulting in the significant enhancement of the mechanical properties. Noted that several iron-rich phases could be observed in the core region under higher super-gravity coefficient. With the formation of the iron-rich phase, the elongation of the alloy decreased slightly. The refinement mechanism of the eutectic structure and the formation mechanism of the iron-rich phase under super-gravity field were discussed in detail. |
|---|