Hot deformation behavior and processing maps of 9Cr3W3Co oxide dispersion-strengthened steel

The hot deformation behavior of as-cast 9Cr3W3Co oxide dispersion-strengthened (ODS) steel was investigated by Gleeble 3500 facility in the temperature range of 900–1,150℃ and at strain rates range of 0.01–10 s−1. The constitutive equation and processing maps were established to describe this comple...

Description complète

Enregistré dans:
Détails bibliographiques
Auteurs principaux: Yang Wen-Sheng, Wang Jia-Wei, Jiang Lei, Wang Tian-Jian, Pei Yu-Bing
Format: article
Langue:EN
Publié: De Gruyter 2021
Sujets:
T
Accès en ligne:https://doaj.org/article/a1d560eca396412fbbf80d3d3b3f94fb
Tags: Ajouter un tag
Pas de tags, Soyez le premier à ajouter un tag!
Description
Résumé:The hot deformation behavior of as-cast 9Cr3W3Co oxide dispersion-strengthened (ODS) steel was investigated by Gleeble 3500 facility in the temperature range of 900–1,150℃ and at strain rates range of 0.01–10 s−1. The constitutive equation and processing maps were established to describe this complex hot deformation process. The true stress–strain curves showed that the softening effects of dynamic recovery and dynamic recrystallization are stronger than the effect of work hardening with further increasing the temperature and strain. The optimal hot working parameters of 9Cr3W3Co-ODS steel are suggested to be T = 1,050–1,100°C and ε̇\dot{\varepsilon } = 0.03–0.3 s−1.