Coplanar-gate ZnO nanowire field emitter arrays with enhanced gate-control performance using a ring-shaped cathode
Abstract Nanowire field emitters have great potential for use as large-area gated field emitter arrays (FEAs). However, the micrometer-scale cathode patterns in gated FEA devices will reduce regulation of the gate voltage and limit the field emission currents of these devices as a result of field-sc...
Guardado en:
| Autores principales: | , , , , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Nature Portfolio
2018
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/ab0cc1f4e293499988f470acd6ce2385 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Abstract Nanowire field emitters have great potential for use as large-area gated field emitter arrays (FEAs). However, the micrometer-scale cathode patterns in gated FEA devices will reduce regulation of the gate voltage and limit the field emission currents of these devices as a result of field-screening effect among the neighboring nanowires. In this article, a ring-shaped ZnO nanowire pad is proposed to overcome this problem. Diode measurements show that the prepared ring-shaped ZnO nanowire pad arrays shows uniform emission with a turn-on field of 5.9 V/µm and a field emission current density of 4.6 mA/cm2 under an applied field of 9 V/µm. The ZnO nanowire pad arrays were integrated into coplanar-gate FEAs and enhanced gate-controlled device characteristics were obtained. The gate-controlled capability was studied via microscopic in-situ measurements of the field emission from the ZnO nanowires in the coplanar-gate FEAs. Based on the results of both simulations and experiments, we attributed the enhanced gate-controlled device capabilities to more efficient emission of electrons from the ZnO nanowires as a result of the increase edge area by designing ring-shaped ZnO nanowire pad. The results are important to the realization of large-area gate-controlled FEAs based on nanowire emitters for use in vacuum electronic devices. |
|---|