Fast oxygen diffusion and iodide defects mediate oxygen-induced degradation of perovskite solar cells

Determining the degradation pathways in lead halide perovskites is key to its development as a viable solar technology. Aristidouet al. identify iodide vacancies as the preferred sites in mediating the photo-induced formation of superoxide species from intercalated oxygen.

Guardado en:

Detalles Bibliográficos
Autores principales:	Nicholas Aristidou, Christopher Eames, Irene Sanchez-Molina, Xiangnan Bu, Jan Kosco, M. Saiful Islam, Saif A. Haque
Formato:	article
Lenguaje:	EN
Publicado:	Nature Portfolio 2017
Materias:	Science Q
Acceso en línea:	https://doaj.org/article/ae45fb55403a4485af29ead3f4b8a884
Etiquetas:	Agregar Etiqueta Sin Etiquetas, Sea el primero en etiquetar este registro!

id	oai:doaj.org-article:ae45fb55403a4485af29ead3f4b8a884
record_format	dspace
spelling	oai:doaj.org-article:ae45fb55403a4485af29ead3f4b8a8842021-12-02T15:38:55ZFast oxygen diffusion and iodide defects mediate oxygen-induced degradation of perovskite solar cells10.1038/ncomms152182041-1723https://doaj.org/article/ae45fb55403a4485af29ead3f4b8a8842017-05-01T00:00:00Zhttps://doi.org/10.1038/ncomms15218https://doaj.org/toc/2041-1723Determining the degradation pathways in lead halide perovskites is key to its development as a viable solar technology. Aristidouet al. identify iodide vacancies as the preferred sites in mediating the photo-induced formation of superoxide species from intercalated oxygen.Nicholas AristidouChristopher EamesIrene Sanchez-MolinaXiangnan BuJan KoscoM. Saiful IslamSaif A. HaqueNature PortfolioarticleScienceQENNature Communications, Vol 8, Iss 1, Pp 1-10 (2017)
institution	DOAJ
collection	DOAJ
language	EN
topic	Science Q
spellingShingle	Science Q Nicholas Aristidou Christopher Eames Irene Sanchez-Molina Xiangnan Bu Jan Kosco M. Saiful Islam Saif A. Haque Fast oxygen diffusion and iodide defects mediate oxygen-induced degradation of perovskite solar cells
description	Determining the degradation pathways in lead halide perovskites is key to its development as a viable solar technology. Aristidouet al. identify iodide vacancies as the preferred sites in mediating the photo-induced formation of superoxide species from intercalated oxygen.
format	article
author	Nicholas Aristidou Christopher Eames Irene Sanchez-Molina Xiangnan Bu Jan Kosco M. Saiful Islam Saif A. Haque
author_facet	Nicholas Aristidou Christopher Eames Irene Sanchez-Molina Xiangnan Bu Jan Kosco M. Saiful Islam Saif A. Haque
author_sort	Nicholas Aristidou
title	Fast oxygen diffusion and iodide defects mediate oxygen-induced degradation of perovskite solar cells
title_short	Fast oxygen diffusion and iodide defects mediate oxygen-induced degradation of perovskite solar cells
title_full	Fast oxygen diffusion and iodide defects mediate oxygen-induced degradation of perovskite solar cells
title_fullStr	Fast oxygen diffusion and iodide defects mediate oxygen-induced degradation of perovskite solar cells
title_full_unstemmed	Fast oxygen diffusion and iodide defects mediate oxygen-induced degradation of perovskite solar cells
title_sort	fast oxygen diffusion and iodide defects mediate oxygen-induced degradation of perovskite solar cells
publisher	Nature Portfolio
publishDate	2017
url	https://doaj.org/article/ae45fb55403a4485af29ead3f4b8a884
work_keys_str_mv	AT nicholasaristidou fastoxygendiffusionandiodidedefectsmediateoxygeninduceddegradationofperovskitesolarcells AT christophereames fastoxygendiffusionandiodidedefectsmediateoxygeninduceddegradationofperovskitesolarcells AT irenesanchezmolina fastoxygendiffusionandiodidedefectsmediateoxygeninduceddegradationofperovskitesolarcells AT xiangnanbu fastoxygendiffusionandiodidedefectsmediateoxygeninduceddegradationofperovskitesolarcells AT jankosco fastoxygendiffusionandiodidedefectsmediateoxygeninduceddegradationofperovskitesolarcells AT msaifulislam fastoxygendiffusionandiodidedefectsmediateoxygeninduceddegradationofperovskitesolarcells AT saifahaque fastoxygendiffusionandiodidedefectsmediateoxygeninduceddegradationofperovskitesolarcells
_version_	1718386068305215488

Fast oxygen diffusion and iodide defects mediate oxygen-induced degradation of perovskite solar cells

Ejemplares similares