Usage of Barkhausen Noise for Assessment of Corrosion Damage on Different Low Alloyed Steels
This study deals with corrosion damage of low alloyed feritic steels of variable strength. Three different steels of nominal yield strength 235, 700 and 1100 MPa were subjected to the variable degree of corrosion attack developed in the corrosion chamber under a neutral salt spray (NSS) atmosphere....
Guardado en:
| Autores principales: | , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
MDPI AG
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/b0c990bfc3704d00b90644743798924c |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | This study deals with corrosion damage of low alloyed feritic steels of variable strength. Three different steels of nominal yield strength 235, 700 and 1100 MPa were subjected to the variable degree of corrosion attack developed in the corrosion chamber under a neutral salt spray (NSS) atmosphere. The corrosion damage was investigated by the use of conventional metallographic observations when the thickness of corroded layer was quantified. Moreover, non-destructive magnetic technique, based on Barkhausen noise, was also employed. It was found that the rate of corrosion damage decreases along with the increasing number of days in the chamber. The similar evolution can be also found for Barkhausen noise emission and the extracted parameters from the emission. It can be reported that conventional rms value of Barkhausen noise signal as well as <i>FWHM</i> (full width at half maximum of Barkhausen noise envelope) can be linked with the corrosion extent, especially in the early phases of corrosion attack. The <i>PP</i> (peak position of Barkhausen noise envelope) values exhibit poor sensitivity. |
|---|